- 熔体流动速率 [g/10min]: 0.5
- 密度 [g/cm3]: 0.92
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.920 g/cc | 0.0332 lb/in³ | ISO 1872/1 |
| Thickness | 38.0 microns | 1.50 mil | |
| Melt Flow | 0.50 g/10 min @Load 2.16 kg | 0.50 g/10 min @Load 4.76 lb | ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
| Film Tensile Strength at Yield, MD | 10.0 MPa | 1450 psi | ISO 1184 |
| Film Tensile Strength at Yield, TD | 11.0 MPa | 1600 psi | ISO 1184 |
| Film Elongation at Break, MD | 600 % | 600 % | ISO 1184 |
| Film Elongation at Break, TD | 790 % | 790 % | ISO 1184 |
| Elmendorf Tear Strength, MD | 6.10 g/micron | 155 g/mil | ASTM D1922 |
| Elmendorf Tear Strength, TD | 14.8 g/micron | 375 g/mil | ASTM D1922 |
| Dart Drop | 4.74 g/micron | 120 g/mil | Calculated from thickness |
| Dart drop Test | 180 g | 0.397 lb | ASTM D1709 |
| Film Tensile Strength at Break, MD | 42.0 MPa | 6090 psi | ISO 1184 |
| Film Tensile Strength at Break, TD | 35.0 MPa | 5080 psi | ISO 1184 |
| Thermal Properties | Metric | English | Comments |
| Vicat Softening Point | 100 °C | 212 °F | ISO 306 |
| Processing Properties | Metric | English | Comments |
| Melt Temperature | 225 °C | 437 °F | |