- 熔体流动速率 [g/10min]: 0.2
- 密度 [g/cm3]: 0.91
- 吸水率 [%]: 0.01
- 缺口冲击强度: 0.427
- 拉伸强度 [MPa]: 7.7
- 断裂伸长率 [%]: 9.03
- 弯曲强度 [MPa]: 2.8
- 弯曲模量 [MPa]: 0.0248
- 热变形温度 [℃]: 40.0
- 脆化温度 [℃]: -85.0
- 透光率 [%]: 50.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.910 - 0.980 g/cc | 0.0329 - 0.0354 lb/in³ | Average value: 0.921 g/cc Grade Count:205 |
| Water Absorption | 0.0100 % | 0.0100 % | Average value: 0.0100 % Grade Count:22 |
| Moisture Absorption at Equilibrium | 0.0100 % | 0.0100 % | Average value: 0.0100 % Grade Count:20 |
| Particle Size | 5.00 - 50.0 µm | 5.00 - 50.0 µm | Average value: 27.5 µm Grade Count:3 |
| Particle Mesh Size | 16.0 - 50.0 Mesh | 16.0 - 50.0 Mesh | Average value: 39.3 Mesh Grade Count:6 |
| Water Vapor Transmission | 15.5 - 18.6 g/m²/day | 0.998 - 1.20 g/100 in²/day | Average value: 17.4 g/m²/day Grade Count:5 |
| Oxygen Transmission | 197 - 200 cc-mm/m²-24hr-atm | 500 - 508 cc-mil/100 in²-24hr-atm | Average value: 199 cc-mm/m²-24hr-atm Grade Count:5 |
| Viscosity | 21000 - 305000 cP @Temperature 190 - 190 °C | 21000 - 305000 cP @Temperature 374 - 374 °F | Average value: 91600 cP Grade Count:8 |
| 21000 - 305000 cP @Shear Rate 300 - 5000 1/s | 21000 - 305000 cP @Shear Rate 300 - 5000 1/s | Average value: 91600 cP Grade Count:8 | |
| Environmental Stress Crack Resistance | 1.00 - 1500 hour | 1.00 - 1500 hour | Average value: 358 hour Grade Count:7 |
| 1.00 - 1.00 hour @Temperature 50.0 - 50.0 °C | 1.00 - 1.00 hour @Temperature 122 - 122 °F | Average value: 1.00 hour Grade Count:2 | |
| 1.00 - 1.00 hour @Thickness 2.00 - 2.00 mm | 1.00 - 1.00 hour @Thickness 0.0787 - 0.0787 in | Average value: 1.00 hour Grade Count:2 | |
| Maximum Moisture Content | 0.100 | 0.100 | Average value: 0.100 Grade Count:3 |
| Thickness | 5.00 - 300 microns | 0.197 - 11.8 mil | Average value: 35.2 microns Grade Count:16 |
| Linear Mold Shrinkage | 0.0100 - 0.0500 cm/cm | 0.0100 - 0.0500 in/in | Average value: 0.0197 cm/cm Grade Count:7 |
| Melt Flow | 0.200 - 2300 g/10 min | 0.200 - 2300 g/10 min | Average value: 36.6 g/10 min Grade Count:177 |
| Base Resin Melt Index | 0.500 - 25.0 g/10 min | 0.500 - 25.0 g/10 min | Average value: 6.32 g/10 min Grade Count:9 |
| Coating Weight | 4.80 - 9.60 g/m² | 3.00 - 6.00 lb/ream | Average value: 6.40 g/m² Grade Count:3 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Shore A | 81.0 - 97.0 | 81.0 - 97.0 | Average value: 91.0 Grade Count:20 |
| Hardness, Shore D | 38.0 - 56.0 | 38.0 - 56.0 | Average value: 48.6 Grade Count:108 |
| Tensile Strength, Ultimate | 2.80 - 56.5 MPa | 406 - 8200 psi | Average value: 11.0 MPa Grade Count:145 |
| Film Tensile Strength at Yield, MD | 12.0 - 30.0 MPa | 1740 - 4350 psi | Average value: 24.2 MPa Grade Count:5 |
| Film Tensile Strength at Yield, TD | 9.00 - 11.0 MPa | 1310 - 1600 psi | Average value: 9.81 MPa Grade Count:7 |
| Tensile Strength, Yield | 7.70 - 136 MPa | 1120 - 19700 psi | Average value: 11.7 MPa Grade Count:146 |
| Film Elongation at Break, MD | 200 - 650 % | 200 - 650 % | Average value: 354 % Grade Count:14 |
| Film Elongation at Break, TD | 550 - 930 % | 550 - 930 % | Average value: 741 % Grade Count:13 |
| Elongation at Break | 13.5 - 800 % | 13.5 - 800 % | Average value: 331 % Grade Count:170 |
| Elongation at Yield | 13.0 - 400 % | 13.0 - 400 % | Average value: 29.5 % Grade Count:34 |
| Modulus of Elasticity | 0.110 - 0.449 GPa | 16.0 - 65.1 ksi | Average value: 0.230 GPa Grade Count:58 |
| Flexural Yield Strength | 9.03 - 48.3 MPa | 1310 - 7000 psi | Average value: 22.1 MPa Grade Count:3 |
| Flexural Modulus | 0.0248 - 1.38 GPa | 3.60 - 200 ksi | Average value: 0.224 GPa Grade Count:95 |
| Secant Modulus | 0.132 - 1.45 GPa | 19.1 - 210 ksi | Average value: 0.270 GPa Grade Count:20 |
| Secant Modulus, MD | 0.138 - 0.234 GPa | 20.0 - 33.9 ksi | Average value: 0.182 GPa Grade Count:12 |
| Secant Modulus, TD | 0.152 - 0.276 GPa | 22.0 - 40.0 ksi | Average value: 0.218 GPa Grade Count:12 |
| Izod Impact, Notched | 0.427 - 5340 J/cm | 0.800 - 10000 ft-lb/in | Average value: 3.48 J/cm Grade Count:10 |
| 0.380 - 1.50 J/cm @Temperature -40.0 - -20.0 °C | 0.712 - 2.81 ft-lb/in @Temperature -40.0 - -4.00 °F | Average value: 0.940 J/cm Grade Count:1 | |
| Izod Impact, Notched (ISO) | 24.0 - 69.4 kJ/m² @Temperature -50.0 - -50.0 °C | 11.4 - 33.0 ft-lb/in² @Temperature -58.0 - -58.0 °F | Average value: 40.5 kJ/m² Grade Count:10 |
| Charpy Impact Unnotched | >= 30.0 J/cm² @Temperature -40.0 - -20.0 °C | >= 143 ft-lb/in² @Temperature -40.0 - -4.00 °F | Average value: 30.0 J/cm² Grade Count:1 |
| Tensile Impact Strength | 200 - 315 kJ/m² | 95.2 - 150 ft-lb/in² | Average value: 263 kJ/m² Grade Count:3 |
| Dart Drop, Total Energy | 24.4048 - 24.4048 J @Temperature -20.0 - -20.0 °C | 18.0000 - 18.0000 ft-lb @Temperature -4.00 - -4.00 °F | Average value: 24.4 J Grade Count:1 |
| Coefficient of Friction | 0.120 - 0.700 | 0.120 - 0.700 | Average value: 0.357 Grade Count:3 |
| Elmendorf Tear Strength, MD | 8.00 - 18.2 g/micron | 203 - 463 g/mil | Average value: 12.4 g/micron Grade Count:7 |
| Elmendorf Tear Strength, TD | 1.84 - 45.8 g/micron | 46.7 - 1160 g/mil | Average value: 14.4 g/micron Grade Count:8 |
| Dart Drop | 2.36 - 30.0 g/micron | 59.9 - 762 g/mil | Average value: 5.87 g/micron Grade Count:13 |
| Dart drop Test | 90.0 - 126 g | 0.198 - 0.278 lb | Average value: 106 g Grade Count:6 |
| Film Tensile Strength at Break, MD | 20.0 - 59.0 MPa | 2900 - 8560 psi | Average value: 30.1 MPa Grade Count:13 |
| Film Tensile Strength at Break, TD | 15.2 - 45.0 MPa | 2200 - 6530 psi | Average value: 22.8 MPa Grade Count:13 |
| Electrical Properties | Metric | English | Comments |
| Electrical Resistivity | 1.00e+15 - 1.00e+16 ohm-cm | 1.00e+15 - 1.00e+16 ohm-cm | Average value: 1.82e+15 ohm-cm Grade Count:22 |
| Surface Resistance | 100 - 1.00e+14 ohm | 100 - 1.00e+14 ohm | Average value: 9.41e+13 ohm Grade Count:17 |
| Dielectric Constant | 2.30 - 2.60 | 2.30 - 2.60 | Average value: 2.36 Grade Count:20 |
| Dissipation Factor | 0.000200 - 0.00300 | 0.000200 - 0.00300 | Average value: 0.000620 Grade Count:20 |
| Comparative Tracking Index | 600 V | 600 V | Average value: 600 V Grade Count:20 |
| Thermal Properties | Metric | English | Comments |
| CTE, linear | 180 - 230 µm/m-°C | 100 - 128 µin/in-°F | Average value: 218 µm/m-°C Grade Count:20 |
| Melting Point | 95.0 - 115 °C | 203 - 238 °F | Average value: 108 °C Grade Count:75 |
| Deflection Temperature at 0.46 MPa (66 psi) | 40.0 - 72.8 °C | 104 - 163 °F | Average value: 44.2 °C Grade Count:23 |
| Deflection Temperature at 1.8 MPa (264 psi) | 38.0 - 101 °C | 100 - 214 °F | Average value: 71.2 °C Grade Count:5 |
| Vicat Softening Point | 52.0 - 117 °C | 126 - 243 °F | Average value: 89.3 °C Grade Count:151 |
| Brittleness Temperature | -85.0 - 0.000 °C | -121 - 32.0 °F | Average value: -52.5 °C Grade Count:80 |
| Flammability, UL94 | HB | HB | Grade Count:20 |
| Oxygen Index | 17.0 % | 17.0 % | Average value: 17.0 % Grade Count:16 |
| Ring & Ball Softening Point | 109 - 130 °C | 228 - 266 °F | Average value: 118 °C Grade Count:4 |
| Shrinkage | 1.00 - 4.00 % | 1.00 - 4.00 % | Average value: 2.45 % Grade Count:6 |
| Optical Properties | Metric | English | Comments |
| Haze | 3.30 - 20.0 % | 3.30 - 20.0 % | Average value: 8.46 % Grade Count:13 |
| Gloss | 7.80 - 83.0 % | 7.80 - 83.0 % | Average value: 58.4 % Grade Count:18 |
| Transmission, Visible | 50.0 - 95.0 % | 50.0 - 95.0 % | Average value: 76.3 % Grade Count:4 |
| Processing Properties | Metric | English | Comments |
| Processing Temperature | 82.2 - 250 °C | 180 - 482 °F | Average value: 160 °C Grade Count:8 |
| Melt Temperature | 105 - 329 °C | 221 - 625 °F | Average value: 197 °C Grade Count:16 |
| Mold Temperature | 15.0 - 65.6 °C | 59.0 - 150 °F | Average value: 36.0 °C Grade Count:10 |
| Injection Pressure | 68.9 - 103 MPa | 10000 - 15000 psi | Average value: 86.2 MPa Grade Count:3 |