- 熔体流动速率 [g/10min]: 0.12
- 密度 [g/cm3]: 0.917
- 吸水率 [%]: 0.01
- 拉伸强度 [MPa]: 8.3
- 弯曲强度 [MPa]: 7.85
- 弯曲模量 [MPa]: 0.214
- 热变形温度 [℃]: 41.0
- 脆化温度 [℃]: -76.0
- 透光率 [%]: 55.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.917 - 1.00 g/cc | 0.0331 - 0.0361 lb/in³ | Average value: 0.923 g/cc Grade Count:324 |
| Water Absorption | 0.0100 % | 0.0100 % | Average value: 0.0100 % Grade Count:17 |
| Moisture Absorption at Equilibrium | 0.0100 % | 0.0100 % | Average value: 0.0100 % Grade Count:17 |
| Water Vapor Transmission | 1.03 - 14.0 g/m²/day | 0.0663 - 0.902 g/100 in²/day | Average value: 10.9 g/m²/day Grade Count:8 |
| Oxygen Transmission Rate | 2000 - 6300 cc/m²/day | 129 - 406 cc/100 in²/day | Average value: 3980 cc/m²/day Grade Count:8 |
| Nitrogen Transmission | 3500 - 7500 cc-mm/m²-24hr-atm | 8890 - 19100 cc-mil/100 in²-24hr-atm | Average value: 4500 cc-mm/m²-24hr-atm Grade Count:4 |
| Environmental Stress Crack Resistance | 168 - 500 hour | 168 - 500 hour | Average value: 263 hour Grade Count:7 |
| Vinyl Acetate Content | 2.50 - 6.60 % | 2.50 - 6.60 % | Average value: 4.60 % Grade Count:13 |
| Thickness | 12.7 - 300 microns | 0.500 - 11.8 mil | Average value: 49.9 microns Grade Count:219 |
| Melt Flow | 0.120 - 60.0 g/10 min | 0.120 - 60.0 g/10 min | Average value: 2.02 g/10 min Grade Count:309 |
| Antiblock Level | 0.000 - 24000 ppm | 0.000 - 24000 ppm | Average value: 2660 ppm Grade Count:36 |
| Slip Level | 0.000 - 1600 ppm | 0.000 - 1600 ppm | Average value: 663 ppm Grade Count:28 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Shore D | 42.0 - 60.0 | 42.0 - 60.0 | Average value: 51.1 Grade Count:30 |
| Tensile Strength, Ultimate | 7.85 - 34.5 MPa | 1140 - 5000 psi | Average value: 12.9 MPa Grade Count:89 |
| Film Tensile Strength at Yield, MD | 6.89 - 28.0 MPa | 1000 - 4060 psi | Average value: 11.0 MPa Grade Count:118 |
| Film Tensile Strength at Yield, TD | 6.21 - 15.9 MPa | 900 - 2300 psi | Average value: 10.9 MPa Grade Count:127 |
| Tensile Strength, Yield | 8.30 - 21.0 MPa | 1200 - 3050 psi | Average value: 11.5 MPa Grade Count:59 |
| Film Elongation at Break, MD | 100 - 640 % | 100 - 640 % | Average value: 323 % Grade Count:269 |
| Film Elongation at Break, TD | 249 - 1420 % | 249 - 1420 % | Average value: 604 % Grade Count:268 |
| Film Elongation at Yield, MD | 5.60 - 330 % | 5.60 - 330 % | Average value: 29.8 % Grade Count:14 |
| Film Elongation at Yield, TD | 5.00 - 520 % | 5.00 - 520 % | Average value: 42.2 % Grade Count:14 |
| Elongation at Break | 50.0 - 1000 % | 50.0 - 1000 % | Average value: 449 % Grade Count:91 |
| Elongation at Yield | 13.0 - 100 % | 13.0 - 100 % | Average value: 27.9 % Grade Count:21 |
| Modulus of Elasticity | 0.160 - 0.442 GPa | 23.2 - 64.1 ksi | Average value: 0.240 GPa Grade Count:71 |
| Flexural Modulus | 0.214 - 0.262 GPa | 31.0 - 38.0 ksi | Average value: 0.236 GPa Grade Count:5 |
| Secant Modulus | 0.130 - 1.35 GPa | 18.9 - 196 ksi | Average value: 0.737 GPa Grade Count:7 |
| Secant Modulus, MD | 0.0600 - 0.366 GPa | 8.70 - 53.1 ksi | Average value: 0.191 GPa Grade Count:198 |
| Secant Modulus, TD | 0.00197 - 0.414 GPa | 0.286 - 60.0 ksi | Average value: 0.218 GPa Grade Count:195 |
| Tensile Impact | 130 - 350 J/cm | 244 - 656 ft-lb/in | Average value: 225 J/cm Grade Count:13 |
| Puncture Energy | 0.203 - 7.00 J | 0.150 - 5.16 ft-lb | Average value: 1.70 J Grade Count:29 |
| Coefficient of Friction | 0.0900 - 1.00 | 0.0900 - 1.00 | Average value: 0.429 Grade Count:142 |
| Tear Strength, Total | 2.00 - 4.00 N | 0.450 - 0.899 lb (f) | Average value: 3.00 N Grade Count:7 |
| Tear Strength | 20.0 - 373 kN/m | 114 - 2130 pli | Average value: 79.8 kN/m Grade Count:15 |
| Elmendorf Tear Strength MD | 8.83 - 1070 g | 8.83 - 1070 g | Average value: 316 g Grade Count:122 |
| Elmendorf Tear Strength TD | 8.34 - 1370 g | 8.34 - 1370 g | Average value: 239 g Grade Count:137 |
| Elmendorf Tear Strength, MD | 1.20 - 15.7 g/micron | 30.5 - 400 g/mil | Average value: 7.69 g/micron Grade Count:136 |
| Elmendorf Tear Strength, TD | 2.10 - 22.2 g/micron | 53.3 - 563 g/mil | Average value: 6.25 g/micron Grade Count:150 |
| Dart Drop | 1.30 - 49.2 g/micron | 33.0 - 1250 g/mil | Average value: 3.71 g/micron Grade Count:159 |
| Dart drop Test | 40.0 - 1500 g | 0.0882 - 3.31 lb | Average value: 178 g Grade Count:217 |
| Film Tensile Strength at Break, MD | 14.0 - 72.0 MPa | 2030 - 10400 psi | Average value: 26.4 MPa Grade Count:257 |
| Film Tensile Strength at Break, TD | 11.0 - 57.0 MPa | 1600 - 8270 psi | Average value: 21.4 MPa Grade Count:255 |
| Heat Seal Strength | 3.00 - 10.8 g/25 mm | 0.00661 - 0.0238 lb/in | Average value: 6.64 g/25 mm Grade Count:13 |
| Heat Seal Strength Initiation Temperature | 100 - 110 °C | 212 - 230 °F | Average value: 106 °C Grade Count:10 |
| Electrical Properties | Metric | English | Comments |
| Electrical Resistivity | 500 - 1.00e+15 ohm-cm | 500 - 1.00e+15 ohm-cm | Average value: 5.48e+14 ohm-cm Grade Count:31 |
| Surface Resistance | 31000 - 1.00e+14 ohm | 31000 - 1.00e+14 ohm | Average value: 5.48e+13 ohm Grade Count:31 |
| Static Decay | 2.00 sec | 2.00 sec | Average value: 2.00 sec Grade Count:13 |
| Dielectric Constant | 2.30 | 2.30 | Average value: 2.30 Grade Count:17 |
| Dissipation Factor | 0.000200 | 0.000200 | Average value: 0.000200 Grade Count:17 |
| Comparative Tracking Index | 600 V | 600 V | Average value: 600 V Grade Count:17 |
| Thermal Properties | Metric | English | Comments |
| CTE, linear | 180 - 230 µm/m-°C | 100 - 128 µin/in-°F | Average value: 206 µm/m-°C Grade Count:17 |
| Melting Point | 107 - 121 °C | 225 - 250 °F | Average value: 112 °C Grade Count:130 |
| Crystallization Temperature | 95.0 - 104 °C | 203 - 219 °F | Average value: 98.4 °C Grade Count:10 |
| Deflection Temperature at 0.46 MPa (66 psi) | 41.0 - 45.0 °C | 106 - 113 °F | Average value: 42.9 °C Grade Count:17 |
| Vicat Softening Point | 85.0 - 107 °C | 185 - 225 °F | Average value: 94.4 °C Grade Count:157 |
| Brittleness Temperature | -76.0 - -38.0 °C | -105 - -36.4 °F | Average value: -73.6 °C Grade Count:40 |
| Flammability, UL94 | HB | HB | Grade Count:17 |
| Oxygen Index | 17.0 % | 17.0 % | Average value: 17.0 % Grade Count:17 |
| Optical Properties | Metric | English | Comments |
| Haze | 1.30 - 27.5 % | 1.30 - 27.5 % | Average value: 8.45 % Grade Count:271 |
| Gloss | 8.20 - 135 % | 8.20 - 135 % | Average value: 68.8 % Grade Count:265 |
| Transmission, Visible | 55.0 - 90.0 % | 55.0 - 90.0 % | Average value: 89.0 % Grade Count:34 |
| Processing Properties | Metric | English | Comments |
| Processing Temperature | 140 - 230 °C | 284 - 446 °F | Average value: 194 °C Grade Count:32 |
| Melt Temperature | 105 - 260 °C | 221 - 500 °F | Average value: 186 °C Grade Count:104 |
| Die Opening | 0.0635 - 0.152 cm | 0.0250 - 0.0600 in | Average value: 0.102 cm Grade Count:17 |
| Blow-up Ratio (BUR) | 1.50 - 4.00 | 1.50 - 4.00 | Average value: 2.42 Grade Count:33 |