- 熔体流动速率 [g/10min]: 5.0
- 密度 [g/cm3]: 0.924
- 拉伸强度 [MPa]: 14.0
- 弯曲模量 [MPa]: 0.300
- 硬度: 46.0
- 热变形温度 [℃]: 42.8
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.924 g/cc | 0.0334 lb/in³ | ASTM D792 |
| Linear Mold Shrinkage | 0.013 cm/cm | 0.013 in/in | MD; ASTM D955 |
| Melt Flow | 5.0 g/10 min | 5.0 g/10 min | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell R | 46 | 46 | ASTM D785 |
| Tensile Strength at Break | 14.0 MPa | 2030 psi | ASTM D638 |
| Tensile Strength, Yield | 14.0 MPa | 2030 psi | ASTM D638 |
| Elongation at Break | >= 500 % | >= 500 % | ASTM D638 |
| Elongation at Yield | >= 400 % | >= 400 % | ASTM D638 |
| Tensile Modulus | 0.297 GPa | 43.1 ksi | ASTM D638 |
| Flexural Strength | 9.03 MPa | 1310 psi | ASTM D790 |
| Flexural Modulus | 0.300 GPa | 43.5 ksi | ASTM D790 |
| Izod Impact, Notched | NB | NB | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
| Deflection Temperature at 0.46 MPa (66 psi) | 42.8 °C | 109 °F | ASTM D648 |