- 熔体流动速率 [g/10min]: 0.35
- 密度 [g/cm3]: 0.932
- 弯曲模量 [MPa]: 0.0820
- 脆化温度 [℃]: -85.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.932 g/cc | 0.0337 lb/in³ | ASTM D1505; ASTM D1928 Proc A |
| Vinyl Acetate Content | 12 % | 12 % | AT Plastics PTM-39 |
| Melt Flow | 0.35 g/10 min @Load 2.16 kg, Temperature 190 °C | 0.35 g/10 min @Load 4.76 lb, Temperature 374 °F | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Shore A | 95 | 95 | ASTM D2240 |
| Hardness, Shore D | 42 | 42 | ASTM D2240 |
| Tensile Strength at Break | 19.0 MPa | 2760 psi | Type IV (50 mm/min); ASTM D638 |
| Elongation at Break | 660 % | 660 % | Type IV (50 mm/min); ASTM D638 |
| Flexural Modulus | 0.0820 GPa | 11.9 ksi | 1% Secant; ASTM D790 |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 97.0 °C | 207 °F | DSC; ASTM D3417 |
| Vicat Softening Point | 78.0 °C | 172 °F | ASTM D1525 |
| Brittleness Temperature | <= -85.0 °C | <= -121 °F | ASTM D746 |