- 熔体流动速率 [g/10min]: 6.0
- 密度 [g/cm3]: 0.949
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.949 g/cc | 0.0343 lb/in³ | ASTM D1505; ASTM D1928 Proc A |
| Vinyl Acetate Content | 28 % | 28 % | AT Plastics PTM-39 |
| Melt Flow | 6.0 g/10 min @Load 2.16 kg, Temperature 190 °C | 6.0 g/10 min @Load 4.76 lb, Temperature 374 °F | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Shore D | 27 | 27 | ASTM D2240 |
| Tensile Strength at Break | 14.0 MPa | 2030 psi | Type IV (50 mm/min); ASTM D638 |
| Elongation at Break | 760 % | 760 % | Type IV (50 mm/min); ASTM D638 |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 71.0 °C | 160 °F | DSC; ASTM D3417 |
| Vicat Softening Point | 43.0 °C | 109 °F | ASTM D1525 |