- 熔体流动速率 [g/10min]: 0.8
- 密度 [g/cm3]: 0.922
- 弯曲模量 [MPa]: 0.269
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.922 g/cc | 0.0333 lb/in³ | AT Plastics PTM-03 |
| Melt Flow | 0.80 g/10 min @Load 2.16 kg, Temperature 190 °C | 0.80 g/10 min @Load 4.76 lb, Temperature 374 °F | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Shore D | 52 | 52 | ASTM D2240 |
| Tensile Strength at Break | 20.0 MPa | 2900 psi | Type IV (50 mm/min); ASTM D638 |
| Elongation at Break | 600 % | 600 % | Type IV (50 mm/min); ASTM D638 |
| Flexural Modulus | 0.269 GPa | 39.0 ksi | 1% Secant; ASTM D790 |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 114 °C | 237 °F | DSC; ASTM D3417 |
| Vicat Softening Point | 99.6 °C | 211 °F | ASTM D1525 |