- 熔体流动速率 [g/10min]: 220.0
- 密度 [g/cm3]: 0.9125
- 弯曲模量 [MPa]: 0.160
- 脆化温度 [℃]: -10.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.9125 g/cc | 0.03297 lb/in³ | AT Plastics PTM-03 |
| Melt Flow | 220 g/10 min @Load 2.16 kg, Temperature 190 °C | 220 g/10 min @Load 4.76 lb, Temperature 374 °F | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Shore A | 95 | 95 | ASTM D2240 |
| Hardness, Shore D | 45 | 45 | ASTM D2240 |
| Tensile Strength at Break | 8.00 MPa | 1160 psi | Type IV (50 mm/min); ASTM D638 |
| Elongation at Break | 100 % | 100 % | Type IV (50 mm/min); ASTM D638 |
| Flexural Modulus | 0.160 GPa | 23.2 ksi | 1% Secant; ASTM D790 |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 100 °C | 212 °F | DSC; ASTM D3417 |
| Vicat Softening Point | 71.2 °C | 160 °F | ASTM D1525 |
| Brittleness Temperature | -10.0 °C | 14.0 °F | ASTM D746 |