- 熔体流动速率 [g/10min]: 2.0
- 密度 [g/cm3]: 0.92
- 拉伸强度 [MPa]: 13.7
- 脆化温度 [℃]: -76.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.920 g/cc | 0.0332 lb/in³ | Base Resin; ASTM D1928/D 1505 |
| ESCR 100% Igepal® | >= 1000 hour | >= 1000 hour | ASTM D1693 |
| ESCR 10% Igepal® | >= 1000 hour | >= 1000 hour | ASTM D1693 |
| Melt Flow | 2.0 g/10 min @Load 2.16 kg, Temperature 190 °C | 2.0 g/10 min @Load 4.76 lb, Temperature 374 °F | Base Resin; ISO 1133 |
| Degree of Crosslinking | 12 % | 12 % | ASTM D2765 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Shore D | 50 | 50 | ASTM D2240 |
| Tensile Strength, Yield | >= 13.7 MPa | >= 1980 psi | Heat Aging (168 hrs at 136°C); ASTM D638 |
| 15.2 MPa | 2200 psi | At 20 in/min; ASTM D1238 | |
| Elongation at Break | <= 75 % | <= 75 % | Hot Creep Test (150°C,29 psi); ICEA T-28-562 |
| 400 % | 400 % | ASTM D638 | |
| Tensile Set | 5.0 % | 5.0 % | Hot Creep Test (150°C,29 psi); ICEA-T-28-562 |
| 360 % | 360 % | Retention; ASTM D638 | |
| Electrical Properties | Metric | English | Comments |
| Electrical Resistivity | 1.00e+15 ohm-cm | 1.00e+15 ohm-cm | ASTM D257 |
| Dielectric Constant | 2.3 @Frequency 60 Hz | 2.3 @Frequency 60 Hz | ASTM D150 |
| Dielectric Strength | >= 21.7 kV/mm @Thickness 1.30 mm | >= 550 kV/in @Thickness 0.0512 in | ASTM D149 |
| Dissipation Factor | 0.00050 @Frequency 60 Hz | 0.00050 @Frequency 60 Hz | ASTM D150 |
| Thermal Properties | Metric | English | Comments |
| Brittleness Temperature | <= -76.0 °C | <= -105 °F | ASTM D746 |