- 熔体流动速率 [g/10min]: 4.5
- 密度 [g/cm3]: 0.928
- 拉伸强度 [MPa]: 9.93
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.928 g/cc | 0.0335 lb/in³ | LE 4481; ASTM D792 |
| 0.933 g/cc | 0.0337 lb/in³ | LE 4437; ASTM D792 | |
| Melt Flow | 4.5 g/10 min | 4.5 g/10 min | LE 4481; ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Yield | >= 9.93 MPa | >= 1440 psi | Heat Aging (7 days at 121°C); ASTM D412 |
| 11.0 MPa | 1600 psi | ASTM D412 | |
| Elongation at Break | <= 50 % | <= 50 % | Hot Creep Test (150°C, .2 MPa); ICEA T-28-562 |
| 225 % | 225 % | Heat Aging (7 days at 121°C); ASTM D412 | |
| 250 % | 250 % | ASTM D412 | |
| Tensile Set | <= 5.0 % | <= 5.0 % | Hot Creep Test (150°C,.2 MPa); ICE T-28-562 |
| Electrical Properties | Metric | English | Comments |
| Electrical Resistivity | 1.00e+16 ohm-cm | 1.00e+16 ohm-cm | ASTM D257 |
| Dielectric Constant | <= 2.7 @Frequency 60 Hz | <= 2.7 @Frequency 60 Hz | ASTM D150 |
| Dielectric Strength | >= 21.7 kV/mm | >= 550 kV/in | ASTM D149 |
| Dissipation Factor | 0.0010 @Frequency 60 Hz | 0.0010 @Frequency 60 Hz | ASTM D150 |
| Processing Properties | Metric | English | Comments |
| Middle Barrel Temperature | >= 140 °C | >= 284 °F | |
| Front Barrel Temperature | >= 120 °C | >= 248 °F | |
| Die Temperature | >= 141 °C | >= 285 °F | |
| Head Temperature | >= 140 °C | >= 284 °F | |