- 熔体流动速率 [g/10min]: 0.75
- 密度 [g/cm3]: 0.923
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.923 g/cc | 0.0333 lb/in³ | ISO 1183 |
| Melt Flow | 0.75 g/10 min @Load 2.16 kg, Temperature 190 °C | 0.75 g/10 min @Load 4.76 lb, Temperature 374 °F | ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
| Film Elongation at Break, MD | 250 % | 250 % | ISO 527-3 |
| Film Elongation at Break, TD | 550 % | 550 % | ISO 527-3 |
| Tensile Modulus | 0.230 GPa | 33.4 ksi | MD; ASTM D882-A |
| 0.260 GPa | 37.7 ksi | TD; ASTM D882-A | |
| Puncture Energy | 2.50 J | 1.84 ft-lb | 66N; ASTM D5748 |
| Coefficient of Friction | 0.80 | 0.80 | Dynamic; ISO 8295 |
| Elmendorf Tear Strength, MD | 10.19 g/micron | 258.8 g/mil | ISO 6383/2 |
| Elmendorf Tear Strength, TD | 5.097 g/micron | 129.5 g/mil | ISO 6383/2 |
| Dart drop Test | 120 g @Thickness 0.0400 mm | 0.265 lb @Thickness 0.00157 in | ISO 7765-1 |
| Film Tensile Strength at Break, MD | 27.0 MPa | 3920 psi | ISO 527-3 |
| Film Tensile Strength at Break, TD | 24.0 MPa | 3480 psi | ISO 527-3 |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 112 °C | 234 °F | ISO 11357-3 |
| Vicat Softening Point | 97.0 °C | 207 °F | ISO 306 |
| Optical Properties | Metric | English | Comments |
| Haze | 8.0 % | 8.0 % | ASTM D1003 |
| Gloss | 85 % | 85 % | ASTM D2457 |