- 熔体流动速率 [g/10min]: 0.7
- 密度 [g/cm3]: 0.921
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 0.921 g/cc | 0.0333 lb/in³ | ASTM D1505 | ||
| Thickness | 38.0 microns | 1.50 mil | |||
| Melt Flow | 0.70 g/10 min @Load 2.16 kg, Temperature 230 °C | 0.70 g/10 min @Load 4.76 lb, Temperature 446 °F | ASTM D1238 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength at Break | 13.0 MPa | 1890 psi | ASTM D638 | ||
| Film Elongation at Break, MD | 363 % | 363 % | ASTM D882 | ||
| Film Elongation at Break, TD | 1331 % | 1331 % | ASTM D882 | ||
| Elongation at Break | 672 % | 672 % | ASTM D638 | ||
| Coefficient of Friction | 0.82 | 0.82 | ASTM D1894 | ||
| Elmendorf Tear Strength, TD | 4.30 g/micron | 109 g/mil | ASTM D1922 | ||
| Dart Drop | 3.44 g/micron | 87.4 g/mil | ASTM D1709 | ||
| Film Tensile Strength at Break, MD | 34.0 MPa | 4930 psi | ASTM D882 | ||
| Film Tensile Strength at Break, TD | 25.0 MPa | 3630 psi | ASTM D882 | ||
| Heat Seal Strength Initiation Temperature | 105 °C | 221 °F | Sealing Initial Temperature; Braskem® Method | ||
| Thermal Properties | Metric | English | Comments | ||
| Vicat Softening Point | 91.0 °C | 196 °F | ASTM D1525 | ||
| Optical Properties | Metric | English | Comments | ||
| Haze | 5.7 % | 5.7 % | ASTM D1003 | ||
| Gloss | 10.8 % | 10.8 % | 60° angle; ASTM D2457 | ||
| Descriptive Properties | |||||
| Minimum Recommended Thickness | 35 µm | ||||