- 熔体流动速率 [g/10min]: 3.8
- 密度 [g/cm3]: 0.922
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 0.922 g/cc | 0.0333 lb/in³ | ASTM-D1505 | ||
| Melt Flow | 3.8 g/10 min @Load 2.16 kg, Temperature 190 °C | 3.8 g/10 min @Load 4.76 lb, Temperature 374 °F | ASTM-D1238 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Film Elongation at Break, MD | 370 % | 370 % | ASTM-D882 | ||
| Film Elongation at Break, TD | 1070 % | 1070 % | ASTM-D882 | ||
| Elmendorf Tear Strength TD | 100 g | 100 g | ASTM-D1922 | ||
| Elmendorf Tear Strength, TD | 2.63 g/micron | 66.8 g/mil | ASTM-D1922 | ||
| Dart Drop | 1.58 g/micron | 40.1 g/mil | ASTM-D1709 | ||
| Dart drop Test | 60.0 g | 0.132 lb | ASTM-D1709 | ||
| Film Tensile Strength at Break, MD | 30.0 MPa | 4350 psi | ASTM-D882 | ||
| Film Tensile Strength at Break, TD | 20.0 MPa | 2900 psi | ASTM-D882 | ||
| Optical Properties | Metric | English | Comments | ||
| Haze | 4.0 % | 4.0 % | ASTM-D1003 | ||
| Gloss | 120 % | 120 % | Angle 60°; ASTM-D2457 | ||
| Processing Properties | Metric | English | Comments | ||
| Die Temperature | 250 - 290 °C | 482 - 554 °F | Cast Film Extrusion | ||
| Mold Temperature | 5.00 - 25.0 °C | 41.0 - 77.0 °F | Injection Molding | ||
| Blow-up Ratio (BUR) | 2.0 - 3.0 | 2.0 - 3.0 | Blown Film Extrusion | ||
| Roll Temperature | 40.0 °C | 104 °F | Chill | ||
| Descriptive Properties | |||||
| Screen Package | 40/60/40 | mesh, Blown Film Extrusion | |||
| Temperature Profile (°C) | 110 | Blown Film Extrusion: 1st zone | |||
| 140 | Blown Film Extrusion: From the screw to the die | ||||
| 150 | Blown Film Extrusion: Die | ||||
| 180-220 | Injection Molding | ||||
| 180-250 | Cast Film Extrusion: Screw | ||||