- 熔体流动速率 [g/10min]: 1.8
- 密度 [g/cm3]: 0.9205
- 弯曲模量 [MPa]: 0.296
- 热变形温度 [℃]: 46.0
- 脆化温度 [℃]: -76.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.9205 g/cc | 0.03326 lb/in³ | ASTM D1505 |
| Melt Flow | 1.8 g/10 min | 1.8 g/10 min | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Shore D | 56 | 56 | ASTM D2240 |
| Tensile Strength at Break | 12.4 MPa | 1800 psi | ASTM D638 |
| Elongation at Break | >= 600 % | >= 600 % | ASTM D638 |
| Flexural Modulus | 0.296 GPa | 43.0 ksi | ASTM D790 |
| Thermal Properties | Metric | English | Comments |
| Deflection Temperature at 0.46 MPa (66 psi) | 46.0 °C | 115 °F | ASTM D648 |
| Vicat Softening Point | 96.0 °C | 205 °F | ASTM D1525 |
| Brittleness Temperature | <= -76.0 °C | <= -105 °F | F50; ASTM D746 |