- 熔体流动速率 [g/10min]: 0.9
- 密度 [g/cm3]: 0.919
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 0.919 g/cc | 0.0332 lb/in³ | ASTM D1505 | ||
| Thickness | 31.8 microns | 1.25 mil | 2:1 BUR; 25 mil die gap | ||
| Melt Flow | 0.90 g/10 min | 0.90 g/10 min | ASTM D1238 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength at Break | 14.5 MPa | 2100 psi | Data derived from type IV specimen, 75 mil plaque @ 20" min.; ASTM D638 | ||
| Film Elongation at Break, MD | 200 % | 200 % | ASTM D882 | ||
| Film Elongation at Break, TD | 500 % | 500 % | ASTM D882 | ||
| Elongation at Break | 660 % | 660 % | Molded; ASTM D638 | ||
| Elmendorf Tear Strength MD | 300 g | 300 g | ASTM D1922 | ||
| Elmendorf Tear Strength TD | 130 g | 130 g | ASTM D1922 | ||
| Dart drop Test | 120 g | 0.265 lb | F50; ASTM D1709 | ||
| Film Tensile Strength at Break, MD | 24.1 MPa | 3500 psi | ASTM D882 | ||
| Film Tensile Strength at Break, TD | 16.5 MPa | 2400 psi | ASTM D882 | ||
| 1% Secant Modulus, MD | 200 MPa | 29000 psi | ASTM D882 | ||
| 1% Secant Modulus, TD | 234 MPa | 34000 psi | ASTM D882 | ||
| Thermal Properties | Metric | English | Comments | ||
| Vicat Softening Point | 92.0 °C | 198 °F | ASTM D1525 | ||
| Processing Properties | Metric | English | Comments | ||
| Melt Temperature | 177 °C | 350 °F | |||
| Descriptive Properties | |||||
| Antiblock | Medium | ||||
| Slip | None | ||||