- 拉伸强度 [MPa]: 22.1
- 弯曲模量 [MPa]: 0.827
- 热变形温度 [℃]: 65.6
- 脆化温度 [℃]: 180.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 0.946 g/cc | 0.946 g/cc | ASTM D1505 |
| ESCR 100% Igepal® | >= 1000 hour | >= 1000 hour | Condition A; ASTM D1693 |
| Melt Index of Compound | 0.25 g/10 min @Temperature 190 °C | 0.25 g/10 min @Temperature 374 °F | ASTM D1505 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Shore D | 70 | 70 | ASTM D2240 |
| Tensile Strength, Yield | 22.1 MPa | 3200 psi | 2"/min; ASTM D638 |
| Elongation at Break | >= 700 % | >= 700 % | 2"/min; ASTM D638 |
| Flexural Modulus | 0.827 GPa | 120 ksi | 2% secant; ASTM D790 |
| Thermal Properties | Metric | English | Comments |
| Deflection Temperature at 0.46 MPa (66 psi) | 65.6 °C | 150 °F | ASTM D648 |
| Brittleness Temperature | 180 °C | 356 °F | ASTM D746 |