- 密度 [g/cm3]: 0.954
- 拉伸强度 [MPa]: 28.3
- 弯曲模量 [MPa]: 1.28
- 脆化温度 [℃]: -75.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.954 g/cc | 0.0345 lb/in³ | ASTM D1505 |
| ESCR 100% Igepal® | 60 hour | 60 hour | Condition B, F50; ASTM D1693 |
| Melt Index of Compound | 0.35 g/10 min @Load 2.16 kg, Temperature 190 °C | 0.35 g/10 min @Load 4.76 lb, Temperature 374 °F | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Yield | 28.3 MPa | 4100 psi | 2" per min, Type IV; ASTM D638 |
| Elongation at Break | >= 500 % | >= 500 % | 2" per min, Type IV; ASTM D638 |
| Flexural Modulus | 1.28 GPa | 185 ksi | ASTM D790 |
| Thermal Properties | Metric | English | Comments |
| Brittleness Temperature | <= -75.0 °C | <= -103 °F | ASTM D746 |