- 熔体流动速率 [g/10min]: 1.3
- 密度 [g/cm3]: 0.934
- 拉伸强度 [MPa]: 18.0
- 脆化温度 [℃]: -80.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.934 g/cc | 0.0337 lb/in³ | ISO 1183/ISO 1872-2B |
| Melt Flow | 1.3 g/10 min @Load 2.16 kg, Temperature 190 °C | 1.3 g/10 min @Load 4.76 lb, Temperature 374 °F | ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Shore D | 47 | 47 | ISO 868 |
| Tensile Strength, Yield | 18.0 MPa | 2610 psi | At 50 mm/min; ISO 527-2 |
| Elongation at Break | >= 700 % | >= 700 % | ISO 527-3 |
| Peel Strength | >= 4.00 kN/m | >= 22.8 pli | 3-layer at 80°C; DIN 30678 |
| >= 20.0 kN/m | >= 114 pli | 3-layer; DIN 30678 | |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 122 °C | 252 °F | ISO 3146 |
| Vicat Softening Point | 100 °C | 212 °F | A50 (10 N); ISO 306 |
| Brittleness Temperature | <= -80.0 °C | <= -112 °F | ASTM D746 |
| Processing Properties | Metric | English | Comments |
| Front Barrel Temperature | 200 - 230 °C | 392 - 446 °F | |
| Die Temperature | 230 - 240 °C | 446 - 464 °F | |
| Melt Temperature | 210 - 230 °C | 410 - 446 °F | |
| Head Temperature | 230 - 240 °C | 446 - 464 °F | |