- 密度 [g/cm3]: 0.48
- 拉伸强度 [MPa]: 13.1
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.480 g/cc | 0.0173 lb/in³ | Expanded Compound; ASTM D792 |
| 0.945 g/cc | 0.0341 lb/in³ | Compound; ASTM D792 | |
| Oxidative Induction Time (OIT) | 50 min | 50 min | At 200°C, Al-pan; ASTM D3895 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Yield | 13.1 MPa | 1900 psi | Expanded Compound; ASTM D638 |
| 22.8 MPa | 3300 psi | Compound; ASTM D638 | |
| Elongation at Break | 500 % | 500 % | Expanded Compound; ASTM D638 |
| 600 % | 600 % | Compound; ASTM D638 | |
| Electrical Properties | Metric | English | Comments |
| Dielectric Constant | 2.33 @Frequency 1e+6 Hz | 2.33 @Frequency 1e+6 Hz | ASTM D1531 |
| Dissipation Factor | 0.000040 @Frequency 1e+6 Hz | 0.000040 @Frequency 1e+6 Hz | ASTM D1531 |