- 熔体流动速率 [g/10min]: 0.7
- 密度 [g/cm3]: 0.945
- 脆化温度 [℃]: -76.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 0.945 g/cc | 0.0341 lb/in³ | ISO 1183/ISO 1872-2 | ||
| Environmental Stress Crack Resistance | >= 48 hour @Temperature 50.0 °C | >= 48 hour @Temperature 122 °F | Igepal 10%; F20; IEC 60811-4-1/B | ||
| Oxidative Induction Time (OIT) | 50 min @Temperature 200 °C | 50 min @Temperature 392 °F | IEC 60811-4-2/B | ||
| Melt Flow | 0.70 g/10 min @Load 2.16 kg, Temperature 190 °C | 0.70 g/10 min @Load 4.76 lb, Temperature 374 °F | ISO 1133 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Hardness, Shore D | 61 | 61 | 1s; ISO 868 | ||
| Tensile Strength at Break | 23.0 MPa | 3340 psi | ISO 527 | ||
| Elongation at Break | 600 % | 600 % | ISO 527-2 | ||
| Electrical Properties | Metric | English | Comments | ||
| Volume Resistivity | 1.00e+6 ohm-cm | 1.00e+6 ohm-cm | IEC 60093 | ||
| Dielectric Constant | 2.33 @Frequency 1.00e+6 Hz | 2.33 @Frequency 1.00e+6 Hz | IEC 60250 | ||
| Dielectric Strength | 22.0 kV/mm | 559 kV/in | IEC 60243 | ||
| Dissipation Factor | 0.000060 @Frequency 1.00e+6 Hz | 0.000060 @Frequency 1.00e+6 Hz | IEC 60250 | ||
| Thermal Properties | Metric | English | Comments | ||
| Brittleness Temperature | <= -76.0 °C | <= -105 °F | ASTM D746 | ||
| Processing Properties | Metric | English | Comments | ||
| Processing Temperature | 100 - 120 °C | 212 - 248 °F | conductor preheating temperature | ||
| Melt Temperature | 220 - 250 °C | 428 - 482 °F | |||
| Die Cooling Temperature | 50.0 °C | 122 °F | water cooling | ||
| Descriptive Properties | |||||
| Petroleum Jelly Absorption (%) | 5 | IEC 60811-4-2 | |||