- 熔体流动速率 [g/10min]: 0.3
- 密度 [g/cm3]: 0.955
- 拉伸强度 [MPa]: 29.0
- 弯曲模量 [MPa]: 1.24
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 0.955 g/cc | 0.0345 lb/in³ | ASTM D-1505 | ||
| ESCR 100% Igepal® | 30 hour | 30 hour | ASTM D-1693 | ||
| Melt Flow | 0.30 g/10 min | 0.30 g/10 min | ASTM D-1238 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength, Yield | 29.0 MPa | 4200 psi | ASTM D-638 | ||
| Elongation at Break | 500 % | 500 % | ASTM D-638 | ||
| Flexural Modulus | 1.24 GPa | 180 ksi | ASTM D-790 | ||
| Descriptive Properties | |||||
| process | Blow Molding | ||||