- 熔体流动速率 [g/10min]: 10.0
- 密度 [g/cm3]: 0.951
- 缺口冲击强度: 12.0
- 拉伸强度 [MPa]: 25.0
- 弯曲模量 [MPa]: 1.273
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 0.951 g/cc | 0.0344 lb/in³ | ASTM D-792 | ||
| ESCR 100% Igepal® | >= 920 hour | >= 920 hour | ASTM D-1693 | ||
| Melt Flow | 10 g/10 min | 10 g/10 min | ASTM D-1238 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength, Yield | 25.0 MPa | 3630 psi | ASTM D-638 | ||
| Elongation at Break | 815 % | 815 % | ASTM D-638 | ||
| Flexural Modulus | 1.273 GPa | 184.6 ksi | ASTM D-790 | ||
| Izod Impact, Notched (ISO) | 12.0 kJ/m² | 5.70 ft-lb/in² | ASTM D-256 | ||
| Descriptive Properties | |||||
| process | Blow Molding | ||||