- 熔体流动速率 [g/10min]: 3.8
- 密度 [g/cm3]: 0.946
- 脆化温度 [℃]: -76.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.946 g/cc | 0.0342 lb/in³ | ISO 1872-2/ISO 1183 |
| Melt Flow | 3.8 g/10 min @Load 5.00 kg, Temperature 140 °C | 3.8 g/10 min @Load 11.0 lb, Temperature 284 °F | ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Shore D | 61 | 61 | 1 second; ISO 868 |
| Tensile Strength at Break | 23.0 MPa | 3340 psi | ISO 527 |
| Elongation at Break | 600 % | 600 % | ISO 527 |
| Thermal Properties | Metric | English | Comments |
| Brittleness Temperature | -76.0 °C | -105 °F | ASTM D746 |
| Processing Properties | Metric | English | Comments |
| Zone 1 | 160 °C | 320 °F | |
| Zone 2 | 170 °C | 338 °F | |
| Zone 3 | 215 °C | 419 °F | |
| Zone 4 | 205 °C | 401 °F | |
| Zone 5 | 210 °C | 410 °F | |
| Die Temperature | 220 °C | 428 °F | |
| Head Temperature | 220 °C | 428 °F | |