- 熔体流动速率 [g/10min]: 0.38
- 密度 [g/cm3]: 0.966
- 拉伸强度 [MPa]: 25.0
- 弯曲模量 [MPa]: 1.781
- 热变形温度 [℃]: 74.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 0.966 g/cc | 0.0349 lb/in³ | ASTM D1505 | ||
| ESCR 100% Igepal® | 36 hour @Thickness 3.00 mm, Temperature 23.0 °C | 36 hour @Thickness 0.118 in, Temperature 73.4 °F | compression molded plaques; ASTM D1693B | ||
| Melt Flow | 0.38 g/10 min @Load 2.16 kg, Temperature 190 °C | 0.38 g/10 min @Load 4.76 lb, Temperature 374 °F | ASTM D1238 | ||
| High Load Melt Index | 42 g/10 min @Load 21.6 kg, Temperature 190 °C | 42 g/10 min @Load 47.6 lb, Temperature 374 °F | ASTM D1238 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Hardness, Shore D | 66 | 66 | ASTM D2240 | ||
| Tensile Strength at Break | 32.0 MPa | 4640 psi | ASTM D638 | ||
| Tensile Strength, Yield | 25.0 MPa | 3630 psi | ASTM D638 | ||
| Flexural Modulus | 1.781 GPa | 258.3 ksi | ASTM D790 | ||
| Thermal Properties | Metric | English | Comments | ||
| Deflection Temperature at 0.46 MPa (66 psi) | 74.0 °C | 165 °F | ASTM D648 | ||
| Vicat Softening Point | 127 °C | 261 °F | ASTM D1525 | ||
| Descriptive Properties | |||||
| Molecular Weight Distribution | Bimodal | ||||