- 熔体流动速率 [g/10min]: 0.7
- 密度 [g/cm3]: 0.954
- 缺口冲击强度: 1.54
- 拉伸强度 [MPa]: 30.0
- 弯曲模量 [MPa]: 1030
- 热变形温度 [℃]: 71.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.954 g/cc | 0.0345 lb/in³ | ASTM-D792 |
| ESCR 100% Igepal® | 520 hour @Thickness 2.00 mm, Temperature 50.0 °C | 520 hour @Thickness 0.0787 in, Temperature 122 °F | 0.3 mm notched-plaques; ASTM-D1693 |
| ESCR 10% Igepal® | 198 hour @Thickness 2.00 mm, Temperature 50.0 °C | 198 hour @Thickness 0.0787 in, Temperature 122 °F | 0.3 mm notched-plaques; ASTM-D1693 |
| Melt Flow | 0.70 g/10 min @Load 5.00 kg, Temperature 190 °C | 0.70 g/10 min @Load 11.0 lb, Temperature 374 °F | ASTM-D1238 |
| 17 g/10 min @Load 21.6 kg, Temperature 190 °C | 17 g/10 min @Load 47.6 lb, Temperature 374 °F | ASTM-D1238 | |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Shore D | 66 | 66 | ASTM-D2240 |
| Tensile Strength at Break | 32.0 MPa | 4640 psi | ASTM-D638 |
| Tensile Strength, Yield | 30.0 MPa | 4350 psi | ASTM-D638 |
| Flexural Modulus, 1% Secant | 1030 MPa | 149000 psi | ASTM-D790 |
| Izod Impact, Notched | 1.54 J/cm | 2.89 ft-lb/in | ASTM-D256 |
| Thermal Properties | Metric | English | Comments |
| Deflection Temperature at 0.46 MPa (66 psi) | 71.0 °C | 160 °F | ASTM-D648 |
| Vicat Softening Point | 128 °C @Load 1.02 kg | 262 °F @Load 2.25 lb | ASTM-D1525 |