- 熔体流动速率 [g/10min]: 11.0
- 密度 [g/cm3]: 0.945
- 拉伸强度 [MPa]: 22.0
- 弯曲模量 [MPa]: 0.900
- 脆化温度 [℃]: -75.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.945 g/cc | 0.0341 lb/in³ | ASTM D1505 |
| ESCR 100% Igepal® | >= 2000 hour | >= 2000 hour | Condition C; ASTM D1693 |
| ESCR 10% Igepal® | >= 2000 hour | >= 2000 hour | Condition B; ASTM D1693 |
| Melt Flow | 11 g/10 min | 11 g/10 min | Condition 190/21.6, HLMI; ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Yield | 22.0 MPa | 3190 psi | 2 in/min, Type IV bar; ASTM D638 |
| Elongation at Break | 800 % | 800 % | 2 in/min, Type IV bar; ASTM D638 |
| Flexural Modulus | 0.900 GPa | 131 ksi | 2% Secant; ASTM D790 |
| Thermal Properties | Metric | English | Comments |
| Brittleness Temperature | <= -75.0 °C | <= -103 °F | Type A clamp, type 1 specimen; ASTM D746 |