- 熔体流动速率 [g/10min]: 0.3
- 密度 [g/cm3]: 0.949
- 拉伸强度 [MPa]: 25.0
- 弯曲模量 [MPa]: 1.171
- 脆化温度 [℃]: -118.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.949 g/cc | 0.0343 lb/in³ | ASTM D1505 |
| Environmental Stress Crack Resistance | 500 hour | 500 hour | Condition A, F50 (100% Igepal) CO-630, ASTM D1693; Condition B, F50: 500, ASTM D1693 |
| Melt Flow | 0.30 g/10 min | 0.30 g/10 min | Condition 190/2.16; ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Yield | 25.0 MPa | 3630 psi | 2 in per min; ASTM D638 Type IV |
| Elongation at Break | >= 600 % | >= 600 % | 2 in per min; ASTM D638 Type IV |
| Flexural Modulus | 1.171 GPa | 169.8 ksi | ASTM D790 |
| Thermal Properties | Metric | English | Comments |
| Brittleness Temperature | <= -118 °C | <= -180 °F | ASTM D746 |
| Processing Properties | Metric | English | Comments |
| Processing Temperature | 171 - 216 °C | 340 - 421 °F | Blow Molding |
| 194 - 216 °C | 381 - 421 °F | Extrusion | |