- 熔体流动速率 [g/10min]: 7.0
- 密度 [g/cm3]: 0.953
- 弯曲模量 [MPa]: 1.24
- 脆化温度 [℃]: -76.1
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.953 g/cc | 0.0344 lb/in³ | ASTM D1505 |
| Melt Flow | 7.0 g/10 min @Load 2.16 kg, Temperature 190 °C | 7.0 g/10 min @Load 4.76 lb, Temperature 374 °F | Procedure A Condition E; ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength at Break | 30.0 MPa | 4350 psi | chs 2 in/min; ASTM D638 |
| Elongation at Break | 950 % | 950 % | ASTM D638 |
| Flexural Modulus | 1.24 GPa | 180 ksi | Test Method I, Procedure B (chs speed 0.05 in/min); ASTM D790 |
| Thermal Properties | Metric | English | Comments |
| Brittleness Temperature | <= -76.1 °C | <= -105 °F | ASTM D746 |