- 密度 [g/cm3]: 0.944
- 缺口冲击强度: 2.14
- 拉伸强度 [MPa]: 22.1
- 弯曲模量 [MPa]: 0.827
- 脆化温度 [℃]: -100.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.944 g/cc | 0.0341 lb/in³ | natural resin; ASTM D792 |
| 0.954 g/cc | 0.0345 lb/in³ | Natural resin extruded under proper conditions with black masterbatch DFNF-0092 (6.5%); ASTM D792 | |
| High Load Melt Index | 8.3 g/10 min @Load 21.6 kg, Temperature 190 °C | 8.3 g/10 min @Load 47.6 lb, Temperature 374 °F | ASTM D1238 |
| Melt Index of Compound | 0.10 g/10 min @Load 2.16 kg, Temperature 190 °C | 0.10 g/10 min @Load 4.76 lb, Temperature 374 °F | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| PENT | 200 hour | 200 hour | Compression molded parts prepared according to ASTM D 1928 Procedure C.; ASTM F1473 |
| Tensile Strength, Yield | 22.1 MPa | 3200 psi | Compression molded parts prepared according to ASTM D 1928 Procedure C.; ASTM D638 |
| Elongation at Break | 850 % | 850 % | Compression molded parts prepared according to ASTM D 1928 Procedure C.; ASTM D638 |
| Flexural Modulus | 0.827 GPa | 120 ksi | Compression molded parts prepared according to ASTM D 1928, method 1, procedure B.; ASTM D790 |
| Izod Impact, Notched | 2.14 J/cm | 4.00 ft-lb/in | Compression molded parts prepared according to ASTM D 1928, method A.; ASTM D256 |
| Thermal Properties | Metric | English | Comments |
| Maximum Service Temperature, Air | >= 250 °C | >= 482 °F | ASTM D3350 |
| Brittleness Temperature | <= -100 °C | <= -148 °F | Compression molded parts prepared according to ASTM D 1928, procedure A.; ASTM D746 |