- 熔体流动速率 [g/10min]: 12.0
- 密度 [g/cm3]: 0.952
- 拉伸强度 [MPa]: 18.6
- 弯曲强度 [MPa]: 18.6
- 弯曲模量 [MPa]: 0.827
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.952 g/cc | 0.0344 lb/in³ | |
| Viscosity | 75000 cP @Shear Rate 5000 1/s, Temperature 190 °C | 75000 cP @Shear Rate 5000 1/s, Temperature 374 °F | Apparent Dynamic Viscosity |
| 160000 cP @Shear Rate 1000 1/s, Temperature 190 °C | 160000 cP @Shear Rate 1000 1/s, Temperature 374 °F | Apparent Dynamic Viscosity | |
| 250000 cP @Shear Rate 300 1/s, Temperature 190 °C | 250000 cP @Shear Rate 300 1/s, Temperature 374 °F | Apparent Dynamic Viscosity | |
| Melt Flow | 12 g/10 min @Load 2.16 kg | 12 g/10 min @Load 4.76 lb | |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Ultimate | 18.6 MPa | 2700 psi | |
| Tensile Strength, Yield | 18.6 MPa | 2700 psi | |
| Elongation at Break | 650 % | 650 % | |
| Modulus of Elasticity | 0.559 GPa | 81.1 ksi | Molded Sample 2% Secant Modulus |
| Flexural Modulus | 0.827 GPa | 120 ksi | |
| Izod Impact Resistance | 7.47 J/cm² | 35.6 ft-lb/in² | |
| Thermal Properties | Metric | English | Comments |
| Vicat Softening Point | 123 °C | 253 °F | |