- 熔体流动速率 [g/10min]: 0.7
- 密度 [g/cm3]: 0.956
- 弯曲强度 [MPa]: 28.0
- 弯曲模量 [MPa]: 1.52
- 脆化温度 [℃]: -85.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.956 g/cc | 0.0345 lb/in³ | ASTM D792 |
| Environmental Stress Crack Resistance | >= 170 hour | >= 170 hour | F50, Condition B, ASTM D1693, 100% Igepal |
| Melt Flow | 0.70 g/10 min @Load 2.16 kg, Temperature 190 °C | 0.70 g/10 min @Load 4.76 lb, Temperature 374 °F | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Ultimate | 28.0 MPa | 4060 psi | ASTM D638 |
| Elongation at Break | 750 % | 750 % | ASTM D638 |
| Flexural Modulus | 1.52 GPa | 220 ksi | ASTM D790 |
| Thermal Properties | Metric | English | Comments |
| Brittleness Temperature | <= -85.0 °C | <= -121 °F | ASTM D696 |
| Processing Properties | Metric | English | Comments |
| Melt Temperature | 160 - 205 °C | 320 - 401 °F | |