- 熔体流动速率 [g/10min]: 8.5
- 密度 [g/cm3]: 0.945
- 缺口冲击强度: 3.7
- 拉伸强度 [MPa]: 22.5
- 弯曲模量 [MPa]: 0.850
- 脆化温度 [℃]: -100.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.945 g/cc | 0.0341 lb/in³ | ASTM D792 |
| Environmental Stress Crack Resistance | >= 5000 hour | >= 5000 hour | F20, Condition C, ASTM D1693, 100% Igepal |
| Melt Flow | 8.5 g/10 min @Load 2.16 kg, Temperature 190 °C | 8.5 g/10 min @Load 4.76 lb, Temperature 374 °F | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Shore D | 60 | 60 | ASTM D2240 |
| Tensile Strength, Yield | 22.5 MPa | 3260 psi | ASTM D638 |
| Elongation at Break | 850 % | 850 % | ASTM D638 |
| Flexural Modulus | 0.850 GPa | 123 ksi | Secant; ASTM D3350 |
| Izod Impact, Notched | 3.70 J/cm | 6.93 ft-lb/in | Notched/Unnotched not specified; ASTM D256 |
| Thermal Properties | Metric | English | Comments |
| CTE, linear | 140 µm/m-°C @Temperature 20.0 °C | 77.8 µin/in-°F @Temperature 68.0 °F | ASTM D696 |
| Melting Point | 128 °C | 262 °F | ASTM D3417 |
| Maximum Service Temperature, Air | 260 °C | 500 °F | Thermal Stability; ASTM D3350 |
| Vicat Softening Point | 124 °C | 255 °F | ASTM D1525 |
| Brittleness Temperature | <= -100 °C | <= -148 °F | ASTM D696 |
| Processing Properties | Metric | English | Comments |
| Melt Temperature | 195 - 225 °C | 383 - 437 °F | |