- 熔体流动速率 [g/10min]: 0.29
- 密度 [g/cm3]: 0.962
- 弯曲模量 [MPa]: 1.48
- 脆化温度 [℃]: -76.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.962 g/cc | 0.0348 lb/in³ | ASTM D1505 |
| Melt Flow | 0.29 g/10 min | 0.29 g/10 min | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Shore D | 68 | 68 | ASTM D2240 |
| Tensile Strength at Break | 30.7 MPa | 4450 psi | ASTM D638 |
| Elongation at Break | 960 % | 960 % | ASTM D638 |
| Flexural Modulus | 1.48 GPa | 215 ksi | ASTM D790 |
| Thermal Properties | Metric | English | Comments |
| Vicat Softening Point | 131 °C | 268 °F | ASTM D1525 |
| Brittleness Temperature | <= -76.0 °C | <= -105 °F | F50; ASTM D746 |