- 密度 [g/cm3]: 1.77
- 吸水率 [%]: 0.02
- 拉伸强度 [MPa]: 44.8
- 弯曲强度 [MPa]: 41.4
- 弯曲模量 [MPa]: 1.72
- 热变形温度 [℃]: 125.0
- 脆化温度 [℃]: -43.3
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.77 - 1.79 g/cc | 0.0639 - 0.0647 lb/in³ | ASTM D792 | ||
| Water Absorption | 0.020 % | 0.020 % | ASTM D570 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Hardness, Shore D | 76 - 80 | 76 - 80 | ASTM D2240 | ||
| Tensile Strength, Ultimate | 41.4 MPa | 6000 psi | ASTM D638 | ||
| Tensile Strength, Yield | 44.8 MPa | 6500 psi | ASTM D638 | ||
| Elongation at Break | 50 - 250 % | 50 - 250 % | ASTM D638 | ||
| Elongation at Yield | 10 % | 10 % | ASTM D638 | ||
| Tensile Modulus | 1.55 GPa | 225 ksi | ASTM D638 | ||
| Flexural Strength | 48.0 - 55.2 MPa | 6960 - 8000 psi | ASTM D790 | ||
| Flexural Modulus | 1.72 GPa | 250 ksi | ASTM D790 | ||
| Compressive Strength | >= 61.0 MPa | >= 8850 psi | ASTM D695 | ||
| Izod Impact, Unnotched | 0.801 - 1.33 J/cm | 1.50 - 2.50 ft-lb/in | ASTM D256 | ||
| Coefficient of Friction | 0.10 - 0.25 | 0.10 - 0.25 | ASTM D1894 | ||
| Coefficient of Friction, Static | 0.15 - 0.25 | 0.15 - 0.25 | ASTM D1894 | ||
| Electrical Properties | Metric | English | Comments | ||
| Volume Resistivity | 1.40e+15 ohm-cm | 1.40e+15 ohm-cm | ASTM D257 | ||
| Dielectric Constant | 6.0 @Frequency 1e+6 Hz | 6.0 @Frequency 1e+6 Hz | ASTM D150 | ||
| 6.8 @Frequency 60 Hz | 6.8 @Frequency 60 Hz | ASTM D150 | |||
| 6.9 @Frequency 1000 Hz | 6.9 @Frequency 1000 Hz | ASTM D150 | |||
| Dielectric Strength | 12.2 kV/mm @Thickness 3.17 mm | 310 kV/in @Thickness 0.125 in | ASTM D149 | ||
| Dissipation Factor | 0.013 @Frequency 1000 Hz | 0.013 @Frequency 1000 Hz | ASTM D150 | ||
| 0.032 @Frequency 60 Hz | 0.032 @Frequency 60 Hz | ASTM D150 | |||
| 0.153 @Frequency 1e+6 Hz | 0.153 @Frequency 1e+6 Hz | ASTM D150 | |||
| Arc Resistance | >= 50 sec | >= 50 sec | ASTM D495 | ||
| Thermal Properties | Metric | English | Comments | ||
| CTE, linear | 101 - 121 µm/m-°C @Temperature 20.0 °C | 56.0 - 67.0 µin/in-°F @Temperature 68.0 °F | ASTM D696 | ||
| Thermal Conductivity | 0.190 - 0.220 W/m-K | 1.32 - 1.53 BTU-in/hr-ft²-°F | ASTM C177 | ||
| Deflection Temperature at 0.46 MPa (66 psi) | 125 - 140 °C | 257 - 284 °F | |||
| Deflection Temperature at 1.8 MPa (264 psi) | 105 - 116 °C | 221 - 240 °F | |||
| Brittleness Temperature | -43.3 °C | -46.0 °F | ASTM D2236 | ||
| Oxygen Index | 43 % | 43 % | ASTM D2863 | ||
| Descriptive Properties | |||||
| Factory Mutual | 4910 Listed | File #3D1Q5.AM | |||