- 密度 [g/cm3]: 2.11
- 缺口冲击强度: 1.3
- 拉伸强度 [MPa]: 15.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 2.11 g/cc | 0.0762 lb/in³ | ISO 1183 |
| Particle Size | 40 µm | 40 µm | Average |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Shore D | 62 | 62 | ISO 868 |
| Ball Indentation Hardness | 48.0 MPa | 6960 psi | ISO 2039-1 |
| Tensile Strength, Yield | 15.0 MPa | 2180 psi | ISO 527 |
| Elongation at Break | 120 % | 120 % | ISO 527 |
| Izod Impact, Notched | 1.30 J/cm | 2.44 ft-lb/in | ISO 180 |
| Thermal Properties | Metric | English | Comments |
| CTE, linear | 65.0 µm/m-°C @Temperature 20.0 °C | 36.1 µin/in-°F @Temperature 68.0 °F | ASTM E 831 |
| Specific Heat Capacity | 1.00 J/g-°C | 0.239 BTU/lb-°F | |
| Thermal Conductivity | 0.250 W/m-K | 1.74 BTU-in/hr-ft²-°F | |
| Melting Point | 237 °C | 459 °F | |
| Flammability, UL94 | V-0 | V-0 | |
| Processing Properties | Metric | English | Comments |
| Processing Temperature | 370 °C | 698 °F | Molding |
| Back Pressure | 40.0 - 60.0 MPa | 5800 - 8700 psi | Molding Pressure |