- 密度 [g/cm3]: 2.16
- 缺口冲击强度: 1.8
- 拉伸强度 [MPa]: 14.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 2.16 g/cc | 0.0780 lb/in³ | ISO 1183 |
| Filler Content | 15 % | 15 % | Graphite |
| Particle Size | 40 µm | 40 µm | Average |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Shore D | 65 | 65 | ISO 868 |
| Ball Indentation Hardness | 52.0 MPa | 7540 psi | ISO 2039-1 |
| Tensile Strength, Yield | 14.0 MPa | 2030 psi | ISO 527 |
| Elongation at Break | 210 % | 210 % | ISO 527 |
| Izod Impact, Notched | 1.80 J/cm | 3.37 ft-lb/in | ISO 180 |
| Electrical Properties | Metric | English | Comments |
| Volume Resistivity | 61 ohm-cm | 61 ohm-cm | 1mA; IEC 60093 |
| Thermal Properties | Metric | English | Comments |
| CTE, linear | 65.0 µm/m-°C @Temperature 20.0 °C | 36.1 µin/in-°F @Temperature 68.0 °F | ASTM E 831 |
| Melting Point | 327 °C | 621 °F | |
| Flammability, UL94 | V-0 | V-0 | |
| Processing Properties | Metric | English | Comments |
| Processing Temperature | 370 °C | 698 °F | Molding |
| Back Pressure | 40.0 - 50.0 MPa | 5800 - 7250 psi | Molding Pressure |