- 密度 [g/cm3]: 1.16
- 吸水率 [%]: 8.5
- 拉伸强度 [MPa]: 84.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.16 g/cc | 0.0419 lb/in³ | ISO 1183 | ||
| Water Absorption | 8.5 % | 8.5 % | ISO 62 | ||
| Moisture Absorption at Equilibrium | 2.9 % | 2.9 % | 23°C/50% R.H.; ISO 62 | ||
| Linear Mold Shrinkage | 0.0080 cm/cm | 0.0080 in/in | ASTM Data; MD | ||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength, Yield | 84.0 MPa | 12200 psi | 50mm/min; ISO 527 | ||
| Elongation at Yield | 3.7 % | 3.7 % | 50mm/min; ISO 527 | ||
| Tensile Modulus | 3.77 GPa | 547 ksi | 1mm/min; ISO 527 | ||
| Charpy Impact Unnotched | 6.90 J/cm² | 32.8 ft-lb/in² | ISO 179 | ||
| Electrical Properties | Metric | English | Comments | ||
| Comparative Tracking Index | 600 V | 600 V | IEC 60112 | ||
| Thermal Properties | Metric | English | Comments | ||
| CTE, linear | 40.0 µm/m-°C @Temperature -30.0 - 30.0 °C | 22.2 µin/in-°F @Temperature -22.0 - 86.0 °F | ASTM Test | ||
| Melting Point | 243 °C | 469 °F | 10 K/min | ||
| 243 °C | 469 °F | ASTM Test | |||
| Deflection Temperature at 1.8 MPa (264 psi) | 68.0 °C | 154 °F | ISO 75 | ||
| Flammability, UL94 | V-0 @Thickness 1.60 mm | V-0 @Thickness 0.0630 in | |||
| V-0 @Thickness 0.400 mm | V-0 @Thickness 0.0157 in | ||||
| Descriptive Properties | |||||
| Color | BK23079 | ||||
| Commercial Status | North America and Europe | ||||
| Impact Modified | No | ||||
| Primary Processing Technique | Injection Molding | ||||