- 密度 [g/cm3]: 1.36
- 吸水率 [%]: 1.3
- 弯曲模量 [MPa]: 8.50
- 热变形温度 [℃]: 215.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.36 g/cc | 0.0491 lb/in³ | ISO 1183 |
| Water Absorption | 1.3 - 2.3 % | 1.3 - 2.3 % | ISO 62 |
| Water Absorption at Saturation | 5.0 - 6.0 % | 5.0 - 6.0 % | ISO 62 |
| Viscosity Measurement | 155 | 155 | Viscosity index; ISO 307 |
| Linear Mold Shrinkage | 0.0040 - 0.012 cm/cm | 0.0040 - 0.012 in/in | FRISETTA Test Method |
| Mechanical Properties | Metric | English | Comments |
| Ball Indentation Hardness | 170 MPa | 24700 psi | ISO 2039-1 |
| Tensile Strength at Break | 160 MPa | 23200 psi | ISO 527 |
| Elongation at Break | 2.5 % | 2.5 % | ISO 527 |
| Tensile Modulus | 10.0 GPa | 1450 ksi | ISO 527 |
| Flexural Strength | 220 MPa | 31900 psi | ISO 178 |
| Flexural Modulus | 8.50 GPa | 1230 ksi | ISO 178 |
| Charpy Impact Unnotched | 2.50 J/cm² | 11.9 ft-lb/in² | DIN 53453 |
| 2.40 J/cm² @Temperature -40.0 °C | 11.4 ft-lb/in² @Temperature -40.0 °F | DIN 53453 | |
| Charpy Impact, Notched | 0.550 J/cm² | 2.62 ft-lb/in² | DIN 53453 |
| Electrical Properties | Metric | English | Comments |
| Volume Resistivity | 1.00e+15 ohm-cm | 1.00e+15 ohm-cm | IEC 93 |
| Dissipation Factor | 0.020 @Frequency 1e+6 Hz | 0.020 @Frequency 1e+6 Hz | IEC 250 |
| Comparative Tracking Index | 550 V | 550 V | CTI 100; IEC 112 |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 242 °C | 468 °F | ISO 3146 DSC |
| Maximum Service Temperature, Air | 120 °C | 248 °F | Continuous; FRISETTA Test Method |
| Deflection Temperature at 0.46 MPa (66 psi) | 215 °C | 419 °F | ISO 75 |
| Deflection Temperature at 1.8 MPa (264 psi) | 180 °C | 356 °F | ISO 75 |