- 密度 [g/cm3]: 1.7
- 吸水率 [%]: 0.4
- 缺口冲击强度: 1.66
- 弯曲模量 [MPa]: 16.5
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.70 g/cc | 0.0614 lb/in³ | ASTM D792 |
| Filler Content | 60 % | 60 % | |
| Water Absorption | 0.40 % | 0.40 % | At 24 hrs; ASTM D570 |
| Linear Mold Shrinkage, Flow | 0.0010 cm/cm | 0.0010 in/in | 0.125 in; ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength at Break | 269 MPa | 39000 psi | ASTM D638 |
| Elongation at Break | 3.0 % | 3.0 % | ASTM D638 |
| Flexural Strength | 400 MPa | 58000 psi | ASTM D790 |
| Flexural Modulus | 16.5 GPa | 2400 ksi | ASTM D790 |
| Izod Impact, Notched | 1.66 J/cm | 3.10 ft-lb/in | 0.125 in; ASTM D256 |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 238 °C | 461 °F | |
| Deflection Temperature at 1.8 MPa (264 psi) | 230 °C | 446 °F | Unannealed; ASTM D648 |