- 密度 [g/cm3]: 1.14
- 吸水率 [%]: 1.9
- 缺口冲击强度: 14.5
- 拉伸强度 [MPa]: 55.0
- 弯曲模量 [MPa]: 1.00
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.14 g/cc | 0.0412 lb/in³ | ISO 1183/A | ||
| Water Absorption | 1.9 % @Temperature 23.0 °C, Time 86400 sec | 1.9 % @Temperature 73.4 °F, Time 24.0 hour | ISO 62 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength, Yield | 55.0 MPa | 7980 psi | ISO 527 type 1 A | ||
| Tensile Modulus | 1.20 GPa | 174 ksi | ISO 527 Type 1A | ||
| Flexural Strength | 50.0 MPa | 7250 psi | ISO 178 | ||
| Flexural Modulus | 1.00 GPa | 145 ksi | ISO 178 | ||
| Izod Impact, Notched (ISO) | 14.5 kJ/m² | 6.90 ft-lb/in² | ISO 180/1eA | ||
| Charpy Impact Unnotched | NB | NB | ISO 179/1eU | ||
| Charpy Impact, Notched | 1.80 J/cm² | 8.57 ft-lb/in² | ISO 179/1eA | ||
| Electrical Properties | Metric | English | Comments | ||
| Volume Resistivity | 1.00e+15 ohm-cm | 1.00e+15 ohm-cm | IEC 60093 | ||
| Surface Resistance | 1.00e+12 ohm | 1.00e+12 ohm | IEC 60093 | ||
| Dielectric Constant | 3.6 | 3.6 | IEC 60250 | ||
| Dissipation Factor | 0.020 | 0.020 | IEC 60250 | ||
| Thermal Properties | Metric | English | Comments | ||
| CTE, linear, Parallel to Flow | 70.0 µm/m-°C @Temperature 23.0 - 85.0 °C | 38.9 µin/in-°F @Temperature 73.4 - 185 °F | ISO 11359 | ||
| Deflection Temperature at 1.8 MPa (264 psi) | 65.0 °C | 149 °F | ISO 75/Af | ||
| Flammability, UL94 | HB @Thickness 1.60 mm | HB @Thickness 0.0630 in | 1210 | ||
| Processing Properties | Metric | English | Comments | ||
| Feed Temperature | 225 - 230 °C | 437 - 446 °F | |||
| Front Barrel Temperature | 235 - 245 °C | 455 - 473 °F | |||
| Melt Temperature | 222 °C | 432 °F | ISO 11357 | ||
| Mold Temperature | 40.0 °C | 104 °F | |||
| Drying Temperature | 80.0 °C | 176 °F | |||
| Moisture Content | <= 0.20 % | <= 0.20 % | |||
| Descriptive Properties | |||||
| Compression Zone | 230-240°C | ||||