- 密度 [g/cm3]: 1.29
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.29 g/cc | 0.0466 lb/in³ | ISO 1183 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength at Break | 140 MPa | 20300 psi | ISO 527-1/-2 |
| Elongation at Break | 4.0 % | 4.0 % | ISO 527-1/-2 |
| Tensile Modulus | 6.10 GPa | 885 ksi | ISO 527-1/-2 |
| Thermal Properties | Metric | English | Comments |
| CTE, linear | 30.0 µm/m-°C @Temperature 20.0 °C | 16.7 µin/in-°F @Temperature 68.0 °F | ISO 11359-1/-2 |
| CTE, linear, Transverse to Flow | 90.0 µm/m-°C @Temperature 20.0 °C | 50.0 µin/in-°F @Temperature 68.0 °F | ISO 11359-1/-2 |
| Melting Point | 295 °C | 563 °F | 10°C/min; ISO 11357-1/-3 |
| Deflection Temperature at 1.8 MPa (264 psi) | 275 °C | 527 °F | ISO 75-1/-2 |