- 密度 [g/cm3]: 1.32
- 吸水率 [%]: 0.04
- 缺口冲击强度: 7.0
- 拉伸强度 [MPa]: 260.0
- 断裂伸长率 [%]: 359
- 弯曲模量 [MPa]: 19.1
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.32 g/cc | 0.0477 lb/in³ | ISO 1183 |
| Water Absorption | 0.040 % @Time 86400 sec | 0.040 % @Time 24.0 hour | ISO 62-1 |
| Linear Mold Shrinkage, Flow | 0.0010 - 0.0020 cm/cm | 0.0010 - 0.0020 in/in | SABIC Method |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Yield | 260 MPa | 37700 psi | 5 mm/min; ISO 527 |
| Elongation at Break | 1.5 % | 1.5 % | 5 mm/min; ISO 527 |
| 2.5 % | 2.5 % | Flexural Strain, break, 2 mm/min; ISO 178 | |
| Tensile Modulus | 25.7 GPa | 3730 ksi | 1 mm/min; ISO 527 |
| Flexural Yield Strength | 359 MPa | 52100 psi | 2 mm/min; ISO 178 |
| Flexural Modulus | 19.1 GPa | 2770 ksi | 2 mm/min; ISO 178 |
| Izod Impact, Notched (ISO) | 7.00 kJ/m² | 3.33 ft-lb/in² | 80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 50.0 kJ/m² | 23.8 ft-lb/in² | 80*10*4; ISO 180/1U |
| Electrical Properties | Metric | English | Comments |
| Surface Resistance | 10 - 1000 ohm | 10 - 1000 ohm | ASTM D257 |
| Thermal Properties | Metric | English | Comments |
| CTE, linear, Parallel to Flow | 520 µm/m-°C @Temperature 23.0 - 60.0 °C | 289 µin/in-°F @Temperature 73.4 - 140 °F | ISO 11359-2 |
| CTE, linear, Transverse to Flow | 56.0 µm/m-°C @Temperature 23.0 - 60.0 °C | 31.1 µin/in-°F @Temperature 73.4 - 140 °F | ISO 11359-2 |