- 吸水率 [%]: 1.3
- 缺口冲击强度: 0.907
- 拉伸强度 [MPa]: 190.0
- 弯曲模量 [MPa]: 9.63
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.40 g/cc | 1.40 g/cc | Method A; ASTM D792 |
| Water Absorption | 1.3 % | 1.3 % | at 24 hrs; ASTM D570 |
| Linear Mold Shrinkage | 0.0040 cm/cm | 0.0040 in/in | ASTM D955 |
| Linear Mold Shrinkage, Transverse | 0.014 cm/cm | 0.014 in/in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength at Break | 190 MPa | 27600 psi | ASTM D638 |
| Tensile Strength, Yield | 190 MPa | 27600 psi | ASTM D638 |
| Elongation at Break | 3.3 % | 3.3 % | ASTM D638 |
| Elongation at Yield | 3.3 % | 3.3 % | ASTM D638 |
| Tensile Modulus | 11.1 GPa | 1610 ksi | ASTM D638 |
| Flexural Strength | 296 MPa | 42900 psi | ASTM D790 |
| Flexural Modulus | 9.63 GPa | 1400 ksi | ASTM D790 |
| Izod Impact, Notched | 0.907 J/cm @Thickness 3.18 mm | 1.70 ft-lb/in @Thickness 0.125 in | ASTM D256 |
| Izod Impact, Unnotched | 11.5 J/cm @Thickness 3.18 mm | 21.5 ft-lb/in @Thickness 0.125 in | ASTM D256 |
| Izod Impact, Notched (ISO) | 9.20 kJ/m² | 4.38 ft-lb/in² | ISO 180 |
| Izod Impact, Unnotched (ISO) | 70.2 kJ/m² | 33.4 ft-lb/in² | ISO 180 |
| Falling Dart Impact | 12.0 J | 8.85 ft-lb | ASTM D3763 |
| Impact Test | 3.29 J | 2.43 ft-lb | Multi-Axial Instrumented Impact Energy; ISO 6603-2 |
| Thermal Properties | Metric | English | Comments |
| Deflection Temperature at 1.8 MPa (264 psi) | 289 °C | 552 °F | Unannealed; ASTM D648 |
| Processing Properties | Metric | English | Comments |
| Melt Temperature | 310 - 321 °C | 590 - 610 °F | |
| Mold Temperature | 82.2 - 121 °C | 180 - 250 °F | |
| Drying Temperature | 82.2 °C | 180 °F | |
| Dry Time | 4 hour | 4 hour | |
| Moisture Content | 0.20 % | 0.20 % | Suggested |
| Back Pressure | 0.172 - 0.345 MPa | 24.9 - 50.0 psi | |