TP Composites HiFill® PA4/6 GF5 IM HS BK 5% Glass Filled物性表参数

TP Composites HiFill® PA4/6 GF5 IM HS BK 5% Glass Filled

TP Composites HiFill® PA4/6 GF5 IM HS BK 5% Glass Filled 物性表: TP Composites HiFill® PA4/6 GF5 IM HS BK 5% Glass Filled物性表及特性介绍,TP Composites HiFill® PA4/6 GF5 IM HS BK 5% Glass Filled注塑参数详情,如需TP Composites HiFill® PA4/6 GF5 IM HS BK 5% Glass Filled下载, 可到相关下载区下载

密度 [g/cm3]: 1.17
吸水率 [%]: 2.6
缺口冲击强度: 0.801
拉伸强度 [MPa]: 48.3
弯曲模量 [MPa]: 2.90

Physical Properties	Metric	English	Comments

Density	1.17 g/cc	0.0423 lb/in³	ASTM D792
Water Absorption	2.6 % @Time 86400 sec	2.6 % @Time 24.0 hour	ASTM D570
Linear Mold Shrinkage, Flow	0.010 cm/cm @Thickness 3.17 mm	0.010 in/in @Thickness 0.125 in	ASTM D955

Mechanical Properties	Metric	English	Comments
Tensile Strength, Yield	48.3 MPa	7000 psi	ASTM D638
Elongation at Break	9.5 %	9.5 %	ASTM D638
Flexural Strength	96.5 MPa	14000 psi	ASTM D790
Flexural Modulus	2.90 GPa	420 ksi	ASTM D790
Izod Impact, Notched	0.801 J/cm @Thickness 3.17 mm	1.50 ft-lb/in @Thickness 0.125 in	ASTM D256

Electrical Properties	Metric	English	Comments
Volume Resistivity	1.00e+11 ohm-cm	1.00e+11 ohm-cm	ASTM D257
Dielectric Strength	27.6 kV/mm	700 kV/in	Method A (Short-Time); ASTM D149

Thermal Properties	Metric	English	Comments
CTE, linear, Parallel to Flow	57.6 µm/m-°C	32.0 µin/in-°F	ASTM D696
Deflection Temperature at 1.8 MPa (264 psi)	160 °C	320 °F	Unannealed; ASTM D648
Flammability, UL94	HB	HB

关键词:
PA46
供应
TP Composites HiFill® PA4/6 GF5 IM HS BK 5% Glass Filled

转载请注明: 转自中国塑胶原料之家 http://www.su-jiao.com/wuxingbiao/

本文链接: http://www.su-jiao.com/yuanliaoku/show-44748.html

免责声明: 本文 TP Composites HiFill® PA4/6 GF5 IM HS BK 5% Glass Filled 仅代表作者个人观点，中国塑胶原料之家无关。中国塑胶原料之家网所转载的内容，其版权均由原作者和资料提供方所拥有！如因作品版权问题需要处理，请与我们联络