- 密度 [g/cm3]: 1.39
- 吸水率 [%]: 2.0
- 缺口冲击强度: 0.747
- 拉伸强度 [MPa]: 193.0
- 弯曲模量 [MPa]: 17.9
- 热变形温度 [℃]: 293.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.39 g/cc | 0.0502 lb/in³ | ASTM D792 |
| Water Absorption | 2.0 % @Time 86400 sec | 2.0 % @Time 24.0 hour | ASTM D570 |
| Linear Mold Shrinkage, Flow | 0.0010 - 0.0030 cm/cm | 0.0010 - 0.0030 in/in | ASTM D955 |
| Linear Mold Shrinkage, Transverse | 0.0040 - 0.0070 cm/cm | 0.0040 - 0.0070 in/in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Yield | 193 MPa | 28000 psi | ASTM D638 |
| Elongation at Break | 2.6 % | 2.6 % | ASTM D638 |
| Flexural Strength | 290 MPa | 42000 psi | ASTM D790 |
| Flexural Modulus | 17.9 GPa | 2600 ksi | ASTM D790 |
| Izod Impact, Notched | 0.747 J/cm @Thickness 3.17 mm | 1.40 ft-lb/in @Thickness 0.125 in | ASTM D256 |
| Electrical Properties | Metric | English | Comments |
| Volume Resistivity | 10 ohm-cm | 10 ohm-cm | ASTM D257 |
| Thermal Properties | Metric | English | Comments |
| CTE, linear, Parallel to Flow | 27.0 µm/m-°C | 15.0 µin/in-°F | ASTM D696 |
| Melting Point | 295 °C | 563 °F | |
| Deflection Temperature at 0.46 MPa (66 psi) | 293 °C | 560 °F | Unannealed; ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 285 °C | 545 °F | Unannealed; ASTM D648 |
| Flammability, UL94 | HB | HB | |