- 熔体流动速率 [g/10min]: 15.0
- 密度 [g/cm3]: 1.04
- 吸水率 [%]: 0.7
- 拉伸强度 [MPa]: 51.5
- 弯曲强度 [MPa]: 50.0
- 弯曲模量 [MPa]: 2.10
- 热变形温度 [℃]: 160.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.04 g/cc | 0.0376 lb/in³ | ISO R1183 |
| Water Absorption | 0.70 % | 0.70 % | 23°C / 24 hrs; ISO 62 |
| Moisture Absorption at Equilibrium | 1.2 % | 1.2 % | 23°C / 50% RH; ISO 62 |
| 2.9 % | 2.9 % | in 23°C water; ISO 62 | |
| Melt Flow | 15 g/10 min @Load 2.16 kg, Temperature 235 °C | 15 g/10 min @Load 4.76 lb, Temperature 455 °F | after drying; ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Shore D | 77 | 77 | ISO 868 |
| Tensile Strength, Ultimate | 50.0 MPa | 7250 psi | ISO R527 |
| Tensile Strength, Yield | 51.5 MPa | 7470 psi | ISO R527 |
| Elongation at Break | >= 100 % | >= 100 % | ISO R527 |
| Elongation at Yield | 4.1 % | 4.1 % | ISO R527 |
| Modulus of Elasticity | 2.60 GPa | 377 ksi | ISO R527 |
| Flexural Strength | 67.0 MPa | 9720 psi | After conditioning at 23°C and 50% RH; ISO 178 |
| 75.0 MPa | 10900 psi | Dry; ISO 178 | |
| Flexural Modulus | 2.10 GPa | 305 ksi | After conditioning at 23°C and 50% RH; ISO 178 |
| 2.30 GPa | 334 ksi | Dry; ISO 178 | |
| Charpy Impact, Notched | 2.00 J/cm² | 9.52 ft-lb/in² | After conditioning at 23°C/50%RH; ISO 179/Af |
| 1.20 J/cm² @Temperature -20.0 °C | 5.71 ft-lb/in² @Temperature -4.00 °F | Dry; ISO 179/Af | |
| 1.30 J/cm² @Temperature -20.0 °C | 6.19 ft-lb/in² @Temperature -4.00 °F | After conditioning at 23°C/50%RH; ISO 179/Af | |
| 1.70 J/cm² @Temperature 23.0 °C | 8.09 ft-lb/in² @Temperature 73.4 °F | Dry; ISO 179/Af | |
| Tensile Creep Modulus, 1 hour | 2270 MPa | 329000 psi | ISO 899-1 |
| Electrical Properties | Metric | English | Comments |
| Volume Resistivity | 6.00e+15 ohm-cm | 6.00e+15 ohm-cm | ASTM D257 |
| Surface Resistance | 2.50e+16 ohm | 2.50e+16 ohm | ASTM D257 |
| Dielectric Strength | 36.0 kV/mm @Thickness 1.00 mm | 914 kV/in @Thickness 0.0394 in | ASTM D149 |
| Dissipation Factor | 0.017 @Frequency 100000 Hz | 0.017 @Frequency 100000 Hz | NFC 26 230 |
| 0.025 @Frequency 100 Hz | 0.025 @Frequency 100 Hz | NFC 26 230 | |
| 0.032 @Frequency 1000 Hz | 0.032 @Frequency 1000 Hz | NFC 26 230 | |
| Comparative Tracking Index | >= 600 V | >= 600 V | NFC 26 220 |
| Thermal Properties | Metric | English | Comments |
| CTE, linear | 65.0 µm/m-°C @Temperature 20.0 - 60.0 °C | 36.1 µin/in-°F @Temperature 68.0 - 140 °F | TMS2 Perkin Elmer |
| CTE, linear, Transverse to Flow | 110 µm/m-°C @Temperature 20.0 - 60.0 °C | 61.1 µin/in-°F @Temperature 68.0 - 140 °F | TMS2 Perkin Elmer |
| Melting Point | 255 °C | 491 °F | ISO R1218 |
| Deflection Temperature at 0.46 MPa (66 psi) | 160 °C | 320 °F | ISO R75 |
| Deflection Temperature at 1.8 MPa (264 psi) | 80.0 °C | 176 °F | ISO R75 |
| Vicat Softening Point | 165 °C | 329 °F | 50 N - B method; ISO 306 |
| 225 °C | 437 °F | 10 N - A method; ISO 306 | |
| Flammability, UL94 | HB | HB | |