- 吸水率 [%]: 2.5
- 缺口冲击强度: 0.49
- 拉伸强度 [MPa]: 57.0
- 弯曲模量 [MPa]: 1.20
- 硬度: 105.0
- 热变形温度 [℃]: 230.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.14 g/cc | 1.14 g/cc | Dry; ASTM D792 |
| Water Absorption | 2.5 % | 2.5 % | Wet |
| Linear Mold Shrinkage | 0.013 - 0.020 cm/cm | 0.013 - 0.020 in/in | Dry; ASTM D2863 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell M | 55 | 55 | Wet; ASTM D785 |
| 80 | 80 | Dry; ASTM D785 | |
| Hardness, Rockwell R | 105 | 105 | Wet; ASTM D785 |
| 120 | 120 | Dry; ASTM D785 | |
| Tensile Strength, Yield | 57.0 MPa | 8270 psi | Wet; ASTM D638 |
| 79.0 MPa | 11500 psi | Dry; ASTM D638 | |
| Elongation at Break | 80 % | 80 % | Dry; ASTM D638 |
| 270 % | 270 % | Wet; ASTM D638 | |
| Flexural Strength | 54.0 MPa | 7830 psi | Wet; ASTM D790 |
| 118 MPa | 17100 psi | Dry; ASTM D790 | |
| Flexural Modulus | 1.20 GPa | 174 ksi | Wet; ASTM D790 |
| 2.80 GPa | 406 ksi | Dry; ASTM D790 | |
| Izod Impact, Notched | 0.490 J/cm | 0.918 ft-lb/in | Dry; ASTM D256 |
| 1.76 J/cm | 3.30 ft-lb/in | Wet; ASTM D256 | |
| Taber Abrasion, mg/1000 Cycles | 5.0 | 5.0 | Wet; ASTM D1044 |
| Thermal Properties | Metric | English | Comments |
| CTE, linear | 80.0 µm/m-°C @Temperature 20.0 °C | 44.4 µin/in-°F @Temperature 68.0 °F | Dry; ASTM D696 |
| Specific Heat Capacity | 1.67 J/g-°C | 0.399 BTU/lb-°F | Dry |
| Thermal Conductivity | 0.200 W/m-K | 1.39 BTU-in/hr-ft²-°F | Dry |
| Deflection Temperature at 0.46 MPa (66 psi) | 230 °C | 446 °F | Dry; ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 70.0 °C | 158 °F | Dry; ASTM D648 |