- 熔体流动速率 [g/10min]: 25.0
- 密度 [g/cm3]: 1.16
- 吸水率 [%]: 2.6
- 拉伸强度 [MPa]: 55.0
- 热变形温度 [℃]: 202.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.16 g/cc | 0.0419 lb/in³ | |
| Water Absorption | 2.6 % | 2.6 % | |
| Moisture Absorption at Equilibrium | 1.1 % | 1.1 % | Humidity Absorption |
| Melt Flow | 25 g/10 min @Load 2.16 kg, Temperature 275 °C | 25 g/10 min @Load 4.76 lb, Temperature 527 °F | |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Yield | 55.0 MPa | 7980 psi | 50 mm/min |
| Elongation at Break | 21 % | 21 % | Nominal Strain; 50 mm/min |
| Elongation at Yield | 2.9 % | 2.9 % | 50 mm/min |
| Tensile Modulus | 2.45 GPa | 355 ksi | 1 mm/min |
| Electrical Properties | Metric | English | Comments |
| Comparative Tracking Index | 600 V | 600 V | |
| Thermal Properties | Metric | English | Comments |
| CTE, linear, Parallel to Flow | 113 µm/m-°C @Temperature 20.0 °C | 62.8 µin/in-°F @Temperature 68.0 °F | |
| CTE, linear, Transverse to Flow | 89.0 µm/m-°C @Temperature 20.0 °C | 49.4 µin/in-°F @Temperature 68.0 °F | |
| Melting Point | 255 °C | 491 °F | 10°C/min |
| Deflection Temperature at 0.46 MPa (66 psi) | 202 °C | 396 °F | |
| Deflection Temperature at 1.8 MPa (264 psi) | 85.0 °C | 185 °F | |
| Vicat Softening Point | 140 °C | 284 °F | 50°C/hr; 50N |
| Flammability, UL94 | HB @Thickness 1.60 mm | HB @Thickness 0.0630 in | |
| HB @Thickness 3.20 mm | HB @Thickness 0.126 in | ||