- 吸水率 [%]: 1.9
- 缺口冲击强度: 1.05
- 拉伸强度 [MPa]: 110.0
- 弯曲模量 [MPa]: 4.70
- 硬度: 120.0
- 热变形温度 [℃]: 260.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.32 g/cc | 1.32 g/cc | Dry; ASTM D792 |
| Water Absorption | 1.9 % | 1.9 % | Wet |
| Linear Mold Shrinkage | 0.0050 cm/cm | 0.0050 in/in | Dry; ASTM D2863 |
| Linear Mold Shrinkage, Transverse | 0.0090 cm/cm | 0.0090 in/in | Dry; ASTM D2863 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell M | 74 | 74 | Wet; ASTM D785 |
| 96 | 96 | Dry; ASTM D785 | |
| Hardness, Rockwell R | 120 | 120 | Dry; ASTM D785 |
| Tensile Strength, Yield | 110 MPa | 16000 psi | Wet; ASTM D638 |
| 180 MPa | 26100 psi | Dry; ASTM D638 | |
| Elongation at Break | 3.0 % | 3.0 % | Dry; ASTM D638 |
| 6.0 % | 6.0 % | Wet; ASTM D638 | |
| Flexural Strength | 175 MPa | 25400 psi | Wet; ASTM D790 |
| 290 MPa | 42100 psi | Dry; ASTM D790 | |
| Flexural Modulus | 4.70 GPa | 682 ksi | Wet; ASTM D790 |
| 8.10 GPa | 1170 ksi | Dry; ASTM D790 | |
| Izod Impact, Notched | 1.05 J/cm | 1.97 ft-lb/in | Dry; ASTM D256 |
| 1.60 J/cm | 3.00 ft-lb/in | Wet; ASTM D256 | |
| Taber Abrasion, mg/1000 Cycles | 12 | 12 | Wet; ASTM D1044 |
| Thermal Properties | Metric | English | Comments |
| CTE, linear | 30.0 µm/m-°C @Temperature 20.0 °C | 16.7 µin/in-°F @Temperature 68.0 °F | Dry; ASTM D696 |
| Thermal Conductivity | 0.300 W/m-K | 2.08 BTU-in/hr-ft²-°F | Dry |
| Deflection Temperature at 0.46 MPa (66 psi) | 260 °C | 500 °F | Dry; ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 250 °C | 482 °F | Dry; ASTM D648 |
| Flammability, UL94 | HB | HB | Dry |