- 吸水率 [%]: 1.6
- 缺口冲击强度: 1.47
- 拉伸强度 [MPa]: 132.0
- 弯曲模量 [MPa]: 5.90
- 硬度: 118.0
- 热变形温度 [℃]: 250.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.50 g/cc | 1.50 g/cc | Dry; ASTM D792 |
| Water Absorption | 1.6 % | 1.6 % | Wet |
| Linear Mold Shrinkage | 0.0030 cm/cm | 0.0030 in/in | Dry; ASTM D2863 |
| Linear Mold Shrinkage, Transverse | 0.0070 cm/cm | 0.0070 in/in | Dry; ASTM D2863 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell M | 93 | 93 | Dry; ASTM D785 |
| Hardness, Rockwell R | 118 | 118 | Dry; ASTM D785 |
| Tensile Strength, Yield | 132 MPa | 19100 psi | Wet; ASTM D638 |
| 186 MPa | 27000 psi | Dry; ASTM D638 | |
| Elongation at Break | 3.0 % | 3.0 % | Dry; ASTM D638 |
| 4.0 % | 4.0 % | Wet; ASTM D638 | |
| Flexural Strength | 177 MPa | 25700 psi | Wet; ASTM D790 |
| 304 MPa | 44100 psi | Dry; ASTM D790 | |
| Flexural Modulus | 5.90 GPa | 856 ksi | Wet; ASTM D790 |
| 11.0 GPa | 1600 ksi | Dry; ASTM D790 | |
| Izod Impact, Notched | 1.47 J/cm | 2.75 ft-lb/in | Dry; ASTM D256 |
| 2.26 J/cm | 4.23 ft-lb/in | Wet; ASTM D256 | |
| Thermal Properties | Metric | English | Comments |
| Deflection Temperature at 0.46 MPa (66 psi) | 250 °C | 482 °F | Dry; ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 240 °C | 464 °F | Dry; ASTM D648 |
| Flammability, UL94 | HB | HB | Dry |